Microfractography of Fish-Eye Fractures in Nitrided Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU93722" target="_blank" >RIV/00216305:26210/11:PU93722 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microfractography of Fish-Eye Fractures in Nitrided Steel

Popis výsledku v původním jazyce

The paper presents results of the micro-fractographical study of fish-eye cracks that were formed in plasma-nitrided specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading regimes. Analysis of the local striation field found near the inclusion in the center of the fish-eye crack together with the local roughness measurements support the hypothesis that the cracks propagate predominantly by mode I micromechanisms. Moreover, the extrapolation of the local crack growth rate curve to the overall fish-eye crack region suggests that similarly to the gigacycle fatigue, the most of the fatigue life is spent on the initiation of the interior microcrack.

Název v anglickém jazyce

Microfractography of Fish-Eye Fractures in Nitrided Steel

Popis výsledku anglicky

The paper presents results of the micro-fractographical study of fish-eye cracks that were formed in plasma-nitrided specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading regimes. Analysis of the local striation field found near the inclusion in the center of the fish-eye crack together with the local roughness measurements support the hypothesis that the cracks propagate predominantly by mode I micromechanisms. Moreover, the extrapolation of the local crack growth rate curve to the overall fish-eye crack region suggests that similarly to the gigacycle fatigue, the most of the fatigue life is spent on the initiation of the interior microcrack.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F08%2FP366" target="_blank" >GP106/08/P366: 3D analýza morfologie povrchů generovaných únavovým zatěžováním</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemické listy

ISSN

0009-2770

e-ISSN

—

Svazek periodika

105

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

721-724

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—