Fractographically-aided Analysis of Fish-eye Crack Growth in Nitrided Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F13%3APU101273" target="_blank" >RIV/00216305:26210/13:PU101273 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fractographically-aided Analysis of Fish-eye Crack Growth in Nitrided Steel

Popis výsledku v původním jazyce

An analysis of the internal fish-eye crack growth in the plasma-nitrided high-strength low-alloy steel specimen has been performed. The study combines information obtained from the fractographical observation of the striations field located near the centre of the fish-eye crack on the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack propagation. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the fatigue crack initiation. This conclusion is consistent with the high cycle and very high cycle fatigue behaviour of specimens without any surface hardening layer.

Název v anglickém jazyce

Fractographically-aided Analysis of Fish-eye Crack Growth in Nitrided Steel

Popis výsledku anglicky

An analysis of the internal fish-eye crack growth in the plasma-nitrided high-strength low-alloy steel specimen has been performed. The study combines information obtained from the fractographical observation of the striations field located near the centre of the fish-eye crack on the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack propagation. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the fatigue crack initiation. This conclusion is consistent with the high cycle and very high cycle fatigue behaviour of specimens without any surface hardening layer.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F0698" target="_blank" >GAP108/10/0698: Nové přístupy k výzkumu únavového šíření trhliny v módech II, III a II+III</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Theoretical and Applied Mechanics

ISSN

1429-2955

e-ISSN

—

Svazek periodika

51

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

8

Strana od-do

439-446

Kód UT WoS článku

000321683200017

EID výsledku v databázi Scopus

—