Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU95868" target="_blank" >RIV/00216305:26210/11:PU95868 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life
Popis výsledku v původním jazyce
An assessment of the residual fatigue life of plasma-nitrided high-strength low-alloy steel specimens has been performed. The study combines fractographical observation of the local striations field found in the centre of the fish-eye crack of the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack growth. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the crack initiation. This conclusion is consistent with the high- and ultra-high-cycle behaviour of specimens without any surface hardening layer.
Název v anglickém jazyce
Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life
Popis výsledku anglicky
An assessment of the residual fatigue life of plasma-nitrided high-strength low-alloy steel specimens has been performed. The study combines fractographical observation of the local striations field found in the centre of the fish-eye crack of the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack growth. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the crack initiation. This conclusion is consistent with the high- and ultra-high-cycle behaviour of specimens without any surface hardening layer.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Zeszyty naukowe politechniki Opolskiej seria Mechanika
ISSN
1429-6055
e-ISSN
—
Svazek periodika
z98
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
10
Strana od-do
1-10
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—