IMPROVEMENT OF WORK ROLL SERVICE LIFE BY MICROSTRUCTURE SIMULATION

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F14%3APU109218" target="_blank" >RIV/00216305:26210/14:PU109218 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

IMPROVEMENT OF WORK ROLL SERVICE LIFE BY MICROSTRUCTURE SIMULATION

Popis výsledku v původním jazyce

The work roll surface in hot rolling mills suffers combined heat and mechanical load. The surface degradation leads to the formation of crack networks. The current research describes a thermal fatigue similar to the governing degradation mechanism, whichcauses the cracks formation perpendicular to surface. This paper describes the additional effect of cyclic thermal loads ? the cause of parallel-to-surface cracks formation within long and thin carbides which is prone to forming inside HiCr steel. The cracks formation is investigated by both a thermal and a structure FEA. These analyses are conducted with a special finite element model which has a steel microstructure. The model is exposed to a thermal load at the end of the rolling gap. The result ? the heterogeneous thermal field is applied like a BC for the structure analysis. The results are presented by a histogram of relative frequency of the first principal stress value, for each microstructure portion separately. The distributi

Název v anglickém jazyce

IMPROVEMENT OF WORK ROLL SERVICE LIFE BY MICROSTRUCTURE SIMULATION

Popis výsledku anglicky

The work roll surface in hot rolling mills suffers combined heat and mechanical load. The surface degradation leads to the formation of crack networks. The current research describes a thermal fatigue similar to the governing degradation mechanism, whichcauses the cracks formation perpendicular to surface. This paper describes the additional effect of cyclic thermal loads ? the cause of parallel-to-surface cracks formation within long and thin carbides which is prone to forming inside HiCr steel. The cracks formation is investigated by both a thermal and a structure FEA. These analyses are conducted with a special finite element model which has a steel microstructure. The model is exposed to a thermal load at the end of the rolling gap. The result ? the heterogeneous thermal field is applied like a BC for the structure analysis. The results are presented by a histogram of relative frequency of the first principal stress value, for each microstructure portion separately. The distributi

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2014, 23rd International Conference on Metallurgy and Materials, Conference Proceedings

ISBN

978-80-87294-54-3

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

Tanger Ltd.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 5. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000350641700045