Charakteristiky stárnutí zeleně svítící Zn2GeO4:Mn tenkovrstvové elektroluminiscnční součástky

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F05%3APU48564" target="_blank" >RIV/00216305:26220/05:PU48564 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Aging characteristics of green-emitting Zn2GeO4:Mn alternating-current thin-film electroluminescent devices

Popis výsledku v původním jazyce

Electrical, electro-optic, temperature, and aging characteristics of green-emittingZn2GeO4:Mn alternating-current thin-film electroluminescent (ACTFEL) devices are presented. The Zn2GeO4:Mn phosphor layers are prepared by rf sputtering. A maximum luminous efficiency of 0.45 lm/W and luminance of 105 cd/m2 at 50 Hz and 40 V above threshold are obtained. Field-ionization of impact-excited Mn+2 luminescent impurities is found to give rise to positive space charge within the Zn2GeO4 phosphor, leading to unnusual device behaviors such as conduction current delay, anomalous positive polarity transient luminance annihilation, transferred charge being comprised of mainly relaxation charge, and a decrease in the 50 Hz threshold voltage with increasing temperature. Low temperature aging experiments suggest that aging is at least partially due to hot electron-induced degradation. Although most Zn2GeO4:Mn ACTFEL devices exhibit a moderate amount of aging, certain devices are found to exhibit no me

Název v anglickém jazyce

Aging characteristics of green-emitting Zn2GeO4:Mn alternating-current thin-film electroluminescent devices

Popis výsledku anglicky

Electrical, electro-optic, temperature, and aging characteristics of green-emittingZn2GeO4:Mn alternating-current thin-film electroluminescent (ACTFEL) devices are presented. The Zn2GeO4:Mn phosphor layers are prepared by rf sputtering. A maximum luminous efficiency of 0.45 lm/W and luminance of 105 cd/m2 at 50 Hz and 40 V above threshold are obtained. Field-ionization of impact-excited Mn+2 luminescent impurities is found to give rise to positive space charge within the Zn2GeO4 phosphor, leading to unnusual device behaviors such as conduction current delay, anomalous positive polarity transient luminance annihilation, transferred charge being comprised of mainly relaxation charge, and a decrease in the 50 Hz threshold voltage with increasing temperature. Low temperature aging experiments suggest that aging is at least partially due to hot electron-induced degradation. Although most Zn2GeO4:Mn ACTFEL devices exhibit a moderate amount of aging, certain devices are found to exhibit no me

Druh

D - Stať ve sborníku

CEP obor

JA - Elektronika a optoelektronika, elektrotechnika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of XXXth Seminary XXX ASR´ 05, Instruments and Control 2005

ISBN

80-248-0774-2

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

10-11

Název nakladatele

VŠB-TU Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

29. 4. 2005

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—