Corrosion-Mechanical Behavior of T91 and 14-19Cr ODS Steels Exposed to Flowing Lead- Bismuth

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F16%3AN0000036" target="_blank" >RIV/26722445:_____/16:N0000036 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/17:N0000086

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.258</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258" target="_blank" >10.4028/www.scientific.net/SSP.258</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Corrosion-Mechanical Behavior of T91 and 14-19Cr ODS Steels Exposed to Flowing Lead- Bismuth

Popis výsledku v původním jazyce

The work describes the behavior of T91 (9Cr ferritic-martensitic steel), MA957 ODS (14%Cr, 0.3Mo, 0.9Ti, 0.25%Y2O3) and PM2000 ODS (19%Cr, 5%Al, 0.25% Y2O3) steels produced by mechanical alloying process, after long-term exposure in liquid lead-bismuth eutectic. Small bend specimens were pre-strained, then exposed to flowing lead-bismuth at 350˚C for 100, 500 and 1000 hours. After exposure the specimens were examined using SEM equipped with EDX. The resulting changes of surface and built-up oxide layers are discussed. Liquid Metal Embrittlement, LME, crack initiation was not observed in any of the specimens. The absence of LME in the condition is discussed.

Název v anglickém jazyce

Corrosion-Mechanical Behavior of T91 and 14-19Cr ODS Steels Exposed to Flowing Lead- Bismuth

Popis výsledku anglicky

The work describes the behavior of T91 (9Cr ferritic-martensitic steel), MA957 ODS (14%Cr, 0.3Mo, 0.9Ti, 0.25%Y2O3) and PM2000 ODS (19%Cr, 5%Al, 0.25% Y2O3) steels produced by mechanical alloying process, after long-term exposure in liquid lead-bismuth eutectic. Small bend specimens were pre-strained, then exposed to flowing lead-bismuth at 350˚C for 100, 500 and 1000 hours. After exposure the specimens were examined using SEM equipped with EDX. The resulting changes of surface and built-up oxide layers are discussed. Liquid Metal Embrittlement, LME, crack initiation was not observed in any of the specimens. The absence of LME in the condition is discussed.

Druh

D - Stať ve sborníku

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechanics of Fracture VIII, Solid State Phenonena, Volume 258

ISBN

978-3-03835-626-4

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

627-630

Název nakladatele

Trans Tech Publications Ltd

Místo vydání

Zurich, Switzerland

Místo konání akce

Brno

Datum konání akce

27. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—