Response to load in liquid lead-bismuth of T91 and 14-19Cr ODS steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F16%3AN0000106" target="_blank" >RIV/26722445:_____/16:N0000106 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/16:N0000107

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Response to load in liquid lead-bismuth of T91 and 14-19Cr ODS steels

Popis výsledku v původním jazyce

The work describes behaviour of T91 (9Cr ferritic-martensitic steel), MA957 ODS (14%Cr, 0.3Mo, 0.9Ti, 0.25%Y2O3 produced by mechanical alloying process) and PM2000 ODS (19%Cr, 5%Al, 0.25% Y2O3) steels after long-term exposures in liquid lead-bismuth eutectic. Small bend specimens (1x3x10 mm3) were pre-stressed according CSN ISO 7539-2 standard and exposed to flowing lead-bismuth melt in the COLONRI I convection loop at 350˚C for 100, 500 and 1000 hours. The content was monitored by using Bi/Bi2O3 ceramic oxygen sensors; the corresponding concentration was in the range 10‑6‑10‑5 wt. %. Then, the specimens were post-test examined using SEM equipped with EDX and microhardness tester. The resulting changes in chemical composition and microhardness close to the surface are discussed. The liquid metal embrittlement crack initiation was not observed and the conditions are commented.

Název v anglickém jazyce

Response to load in liquid lead-bismuth of T91 and 14-19Cr ODS steels

Popis výsledku anglicky

The work describes behaviour of T91 (9Cr ferritic-martensitic steel), MA957 ODS (14%Cr, 0.3Mo, 0.9Ti, 0.25%Y2O3 produced by mechanical alloying process) and PM2000 ODS (19%Cr, 5%Al, 0.25% Y2O3) steels after long-term exposures in liquid lead-bismuth eutectic. Small bend specimens (1x3x10 mm3) were pre-stressed according CSN ISO 7539-2 standard and exposed to flowing lead-bismuth melt in the COLONRI I convection loop at 350˚C for 100, 500 and 1000 hours. The content was monitored by using Bi/Bi2O3 ceramic oxygen sensors; the corresponding concentration was in the range 10‑6‑10‑5 wt. %. Then, the specimens were post-test examined using SEM equipped with EDX and microhardness tester. The resulting changes in chemical composition and microhardness close to the surface are discussed. The liquid metal embrittlement crack initiation was not observed and the conditions are commented.

Druh

D - Stať ve sborníku

CEP obor

JF - Jaderná energetika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Utilization of SUSEN Technologies for the Gen IV Development

ISBN

978-80-270-0925-1

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

75-81

Název nakladatele

Centrum výzkumu Řež, s.r.o.

Místo vydání

Řež

Místo konání akce

Řež

Datum konání akce

24. 11. 2016

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—