Non-destructive measurement of material degradation for component life prediction

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F03%3ASKOVYZ05" target="_blank" >RIV/47718684:_____/03:SKOVYZ05 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Non-destructive measurement of material degradation for component life prediction

Popis výsledku v původním jazyce

The final report summarizes the results of an evaluation a non-destructive technique for detection in service material deterioration on the basis of electrochemical measurements developed within the CZ2 project: "Non-destructive measurement of material degradation for coponent life prediction", performed by ŠKODA VÝZKUM s.r.o. as a part of the COST 522 program on materials for advanced steam cycles. Zhe paper describes the results of an investigation of the electrochemical polarization characteristics of the new cast and forged creep resisting 9% Cr steels, from the COST 501 and 522 programs, in the state "as received" and after creep tests. A long-term exploitation causes changes in shapes of polarization curves. These changes are due more to the effect of temperature than to the applied stress and they seem to be connected with microstructural phase evolution and material degradation.

Název v anglickém jazyce

Non-destructive measurement of material degradation for component life prediction

Popis výsledku anglicky

The final report summarizes the results of an evaluation a non-destructive technique for detection in service material deterioration on the basis of electrochemical measurements developed within the CZ2 project: "Non-destructive measurement of material degradation for coponent life prediction", performed by ŠKODA VÝZKUM s.r.o. as a part of the COST 522 program on materials for advanced steam cycles. Zhe paper describes the results of an investigation of the electrochemical polarization characteristics of the new cast and forged creep resisting 9% Cr steels, from the COST 501 and 522 programs, in the state "as received" and after creep tests. A long-term exploitation causes changes in shapes of polarization curves. These changes are due more to the effect of temperature than to the applied stress and they seem to be connected with microstructural phase evolution and material degradation.

Druh

V_x - Nezařazeno - Výzkumná zpráva obsahující utajované informace (takový výsledek lze do RIV vložit pouze v případě, že zpráva obsahuje utajované informace a pole R12 = U), nebo souhrnná výzkumná zpráva

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20522.70" target="_blank" >OC 522.70: Nedestruktivní měření degradace materiálových vlastností pro odhad zbytkové životnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

C - Předmět řešení projektu podléhá obchodnímu tajemství (§ 504 Občanského zákoníku), ale název projektu, cíle projektu a u ukončeného nebo zastaveného projektu zhodnocení výsledku řešení projektu (údaje P03, P04, P15, P19, P29, PN8) dodané do CEP, jsou upraveny tak, aby byly zveřejnitelné.

Počet stran výsledku

27

Místo vydání

Plzeň

Název nakladatele resp. objednatele

ŠKODA VÝZKUM s.r.o.

Verze

—