Analysis of Cracked Rail of the Crane of Type A120

Popis výsledku v původním jazyce

The aim of the work was to find out the causes of cracking of the A120 crane track rail. Although the track was regularly inspected by defectoscopic techniques, after five years of operation, the rail was broken at the weldment. The elemental composition of the welded joint materials was verified and the mechanical properties were determined. A fractographic description of the fracture surface was performed and the structure of the material was evaluated. Several factors contributed to the formation of crack, the combination of which led to a rail failure. Defects of the welded joint, acting as notches, from which they initiated fatigue cracks, unfavourable microstructure of the weld metal, low toughness of the base material and operating environment and conditions were dominant.

Název v anglickém jazyce

Analysis of Cracked Rail of the Crane of Type A120

Popis výsledku anglicky

The aim of the work was to find out the causes of cracking of the A120 crane track rail. Although the track was regularly inspected by defectoscopic techniques, after five years of operation, the rail was broken at the weldment. The elemental composition of the welded joint materials was verified and the mechanical properties were determined. A fractographic description of the fracture surface was performed and the structure of the material was evaluated. Several factors contributed to the formation of crack, the combination of which led to a rail failure. Defects of the welded joint, acting as notches, from which they initiated fatigue cracks, unfavourable microstructure of the weld metal, low toughness of the base material and operating environment and conditions were dominant.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20301 - Mechanical engineering

Projekt

<a href="/cs/project/TN01000007" target="_blank" >TN01000007: Národní centrum pro energetiku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Přínos metalografie pro řešení výrobních problémů

ISBN

978-80-01-06883-0

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

257-254

Název nakladatele

České vysoké učení technické v Praze

Místo vydání

Praha

Místo konání akce

Mariánské Lázně

Datum konání akce

21. 9. 2021

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—