Analysis of 42SiCr steel after Quenching and Partitioning by Laser Scanning Confocal Microscopy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F10%3A00504814" target="_blank" >RIV/49777513:23210/10:00504814 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of 42SiCr steel after Quenching and Partitioning by Laser Scanning Confocal Microscopy

Popis výsledku v původním jazyce

The effect of heat treatment conditions on the microstructure and properties of low-alloyed 42SiCr steel is described with the use of a Laser Scanning Confocal Microscope (LSCM) as the main tool for analysing the final microstructures after different heat treatment strategies and fracture surfaces after mechanical testing. 42SiCr steel possesses in a basic state pearlitic-ferritic microstructure with strength of 980 MPa and ductility of 30%. Conventional treatment of this steel increases its strength, but the ductility drops down to several per cent. A new Q-P (Quenching & Partitioning) treatment, consisting of austenisation of steel, undercooling to a temperature between Ms and Mf, and subsequent annealing at slightly elevated temperatures, has been developed to increase both strength and ductility of steel. This is enabled due to the final microstructures of the steel made of cubic martensite matrix with 5-15% of stabilised retained austenite. The influence of various parameter

Název v anglickém jazyce

Analysis of 42SiCr steel after Quenching and Partitioning by Laser Scanning Confocal Microscopy

Popis výsledku anglicky

The effect of heat treatment conditions on the microstructure and properties of low-alloyed 42SiCr steel is described with the use of a Laser Scanning Confocal Microscope (LSCM) as the main tool for analysing the final microstructures after different heat treatment strategies and fracture surfaces after mechanical testing. 42SiCr steel possesses in a basic state pearlitic-ferritic microstructure with strength of 980 MPa and ductility of 30%. Conventional treatment of this steel increases its strength, but the ductility drops down to several per cent. A new Q-P (Quenching & Partitioning) treatment, consisting of austenisation of steel, undercooling to a temperature between Ms and Mf, and subsequent annealing at slightly elevated temperatures, has been developed to increase both strength and ductility of steel. This is enabled due to the final microstructures of the steel made of cubic martensite matrix with 5-15% of stabilised retained austenite. The influence of various parameter

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2010

ISBN

978-80-87294-17-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

TANGER

Místo vydání

Ostrava

Místo konání akce

Rožnov pod Radhoštěm

Datum konání akce

1. 1. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—