Microstructure of TiAlSiN Coatings Prepared by Cathodic arc PVD

Popis výsledku v původním jazyce

Films of TiAlSiN were deposited on cold working tool steel, prepared by powder metallurgy, substrates by a commercial cathodic arc-plasma deposition system. Presence of TiN and AlN crystal phase was found on films, but no XRD peaks related to Al and Si were found. Hardness, morphology and adhesion of films changed with different deposition parameters. Hardness and modulus of prepared coatings were measured by nanoindentation with Nanoindenter XP Maximum hardness (39.44GPa) of films was found on sample with ratio Al:Ti:Si 1:1:0.1.

Název v anglickém jazyce

Microstructure of TiAlSiN Coatings Prepared by Cathodic arc PVD

Popis výsledku anglicky

Films of TiAlSiN were deposited on cold working tool steel, prepared by powder metallurgy, substrates by a commercial cathodic arc-plasma deposition system. Presence of TiN and AlN crystal phase was found on films, but no XRD peaks related to Al and Si were found. Hardness, morphology and adhesion of films changed with different deposition parameters. Hardness and modulus of prepared coatings were measured by nanoindentation with Nanoindenter XP Maximum hardness (39.44GPa) of films was found on sample with ratio Al:Ti:Si 1:1:0.1.

Druh

O - Ostatní výsledky

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/ED2.1.00%2F03.0088" target="_blank" >ED2.1.00/03.0088: Centrum nových technologií a materiálů (CENTEM)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů