Studies on the Mechanical Properties of C45 Steel with Martensitic Structure after a High Tempering Process

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F22%3A43965210" target="_blank" >RIV/49777513:23210/22:43965210 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.astrj.com/Studies-on-the-Mechanical-Properties-of-C45-Steel-with-Martensitic-Structure-after,150564,0,2.html" target="_blank" >http://www.astrj.com/Studies-on-the-Mechanical-Properties-of-C45-Steel-with-Martensitic-Structure-after,150564,0,2.html</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.12913/22998624/150564" target="_blank" >10.12913/22998624/150564</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Studies on the Mechanical Properties of C45 Steel with Martensitic Structure after a High Tempering Process

Popis výsledku v původním jazyce

This article describes the studies of the mechanical properties of the martensitic structure of C45 steel, obtained as a result of heat treatment. This steel was subjected to high tempering, within the temperature range of 500÷700°C (every 50°C) and for various exposure times, from 15 minutes to 23 hours. Moreover, martensitic steel was sub- jected to tests by quenching at a temperature of 850°C for 20 minutes and then tempering it for 1 hour, within the temperature range of 50÷800°C (every 50°C). The resulting steel samples were subjected to strength tests, that is, to tensile and hardness tests and also to tests on the micro-structure. The results of these studies are presented and discussed, in detail, in terms of their practical application.

Název v anglickém jazyce

Studies on the Mechanical Properties of C45 Steel with Martensitic Structure after a High Tempering Process

Popis výsledku anglicky

This article describes the studies of the mechanical properties of the martensitic structure of C45 steel, obtained as a result of heat treatment. This steel was subjected to high tempering, within the temperature range of 500÷700°C (every 50°C) and for various exposure times, from 15 minutes to 23 hours. Moreover, martensitic steel was sub- jected to tests by quenching at a temperature of 850°C for 20 minutes and then tempering it for 1 hour, within the temperature range of 50÷800°C (every 50°C). The resulting steel samples were subjected to strength tests, that is, to tensile and hardness tests and also to tests on the micro-structure. The results of these studies are presented and discussed, in detail, in terms of their practical application.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20301 - Mechanical engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Advances in Science and Technology Research Journal

ISSN

2299-8624

e-ISSN

2299-8624

Svazek periodika

16

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

10

Strana od-do

306-315

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85132108409