Soldering steel sheets using soft solders

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41310%2F13%3A61927" target="_blank" >RIV/60460709:41310/13:61927 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Soldering steel sheets using soft solders

Popis výsledku v původním jazyce

The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Sn63Pb37, Sn60Pb40, Pb60Sn40 and Pb48Sn32Bi and leadless soft solders types Sn96Ag4, Sn99Cu1, Sn70Zn30 and Sn96Ag3Cu1 were used. As basic joint material steel sheet of 1.0 mm thickness and zinc-coated steel sheet of 1.0 mm thickness were used. The size of test specimen was 100 x 20 mm. Two sheets were always cleaned and jointed together. For heating the propane-butane plus airflame was used. The tested assemblies were loaded using the universal tensile-strength testing machine until their failure. At the tests the force needed for assemblies' failure and failure type (in the soldered joint, in the basic material) was recordedand the solder strength was calculated from the measured data. The test results show that for soldering of steel sheets as well of zinc-coated steel sheets of 1.0 mm thickness the joints soldered using the lead soft solder type Sn63Pb37

Název v anglickém jazyce

Soldering steel sheets using soft solders

Popis výsledku anglicky

The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Sn63Pb37, Sn60Pb40, Pb60Sn40 and Pb48Sn32Bi and leadless soft solders types Sn96Ag4, Sn99Cu1, Sn70Zn30 and Sn96Ag3Cu1 were used. As basic joint material steel sheet of 1.0 mm thickness and zinc-coated steel sheet of 1.0 mm thickness were used. The size of test specimen was 100 x 20 mm. Two sheets were always cleaned and jointed together. For heating the propane-butane plus airflame was used. The tested assemblies were loaded using the universal tensile-strength testing machine until their failure. At the tests the force needed for assemblies' failure and failure type (in the soldered joint, in the basic material) was recordedand the solder strength was calculated from the measured data. The test results show that for soldering of steel sheets as well of zinc-coated steel sheets of 1.0 mm thickness the joints soldered using the lead soft solder type Sn63Pb37

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JR - Ostatní strojírenství

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Research in Agricultural Engineering (Zemědělská technika)

ISSN

1212-9151

e-ISSN

—

Svazek periodika

59

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

141-146

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—