Soldering sheets using soft solders

Popis výsledku v původním jazyce

The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Pb60Sn40 and Sn60Pb40 and leadless soft solders types Sn95.5Ag3.8Cu0.7 and Sn96Ag4 were used. As basic materials steel sheet,zinc-coated steel sheet, copper sheet and brass sheet 100 x 20 x 1 mm was the test samples size. Always two sheets were cleaned and jointed together. For heating the propane-butane + air flame was used. Then the tested assemblies were loaded using the universal tensile-strength testing machine till to failure. At the tests the force needed for assemblies failure and failure type (in soldered joint, in basic material) were recorded. From measured data the solder strength was calculated. From the experiment results it follows that from the point of view of the soldered joints strength as well of the solder strength relatively small differences were found. At the same time it is evident that the joint strength and solder strength depend on

Název v anglickém jazyce

Soldering sheets using soft solders

Popis výsledku anglicky

The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Pb60Sn40 and Sn60Pb40 and leadless soft solders types Sn95.5Ag3.8Cu0.7 and Sn96Ag4 were used. As basic materials steel sheet,zinc-coated steel sheet, copper sheet and brass sheet 100 x 20 x 1 mm was the test samples size. Always two sheets were cleaned and jointed together. For heating the propane-butane + air flame was used. Then the tested assemblies were loaded using the universal tensile-strength testing machine till to failure. At the tests the force needed for assemblies failure and failure type (in soldered joint, in basic material) were recorded. From measured data the solder strength was calculated. From the experiment results it follows that from the point of view of the soldered joints strength as well of the solder strength relatively small differences were found. At the same time it is evident that the joint strength and solder strength depend on

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JR - Ostatní strojírenství

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis

ISSN

1211-8516

e-ISSN

—

Svazek periodika

61

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

1597-1604

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—