Tepelná stabilita indexu lomu PMMA vrstev připravených pod elektrickým polem

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F07%3A00020207" target="_blank" >RIV/60461373:22310/07:00020207 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Thermal stability of refractive index of polymethylmethacrylate layers prepared under electrical field

Popis výsledku v původním jazyce

Thin films of polymethylmethacrylate (PMMA) were prepared by spin-coating with and without assistance of electrical field. Refractive index of the films was studied as a function of PMMA molecular weight and the time of specimen aging proceeding at different temperatures. The PMMA aging rate was modified by addition of non-polar polystyrene (PS). Refractive index and the aging rate of the films prepared under electrical field are inversely proportional to PMMA molecular weight. From calculated activation energy it is speculated that observed reorientation of PMMA macromolecules at elevated temperature is mostly due to a movement of side polar groups. Thermal stability of films composed of PMMA and PS increases with increasing fraction of PS. No measurable change of refractive index of the PMMA films with 4?10 wt.% PS admixture was observed even after 330 h of aging at 363 K, so that in these films no reorientation of PMMA dipoles occurs. Such films are considered as prospective materia

Název v anglickém jazyce

Thermal stability of refractive index of polymethylmethacrylate layers prepared under electrical field

Popis výsledku anglicky

Thin films of polymethylmethacrylate (PMMA) were prepared by spin-coating with and without assistance of electrical field. Refractive index of the films was studied as a function of PMMA molecular weight and the time of specimen aging proceeding at different temperatures. The PMMA aging rate was modified by addition of non-polar polystyrene (PS). Refractive index and the aging rate of the films prepared under electrical field are inversely proportional to PMMA molecular weight. From calculated activation energy it is speculated that observed reorientation of PMMA macromolecules at elevated temperature is mostly due to a movement of side polar groups. Thermal stability of films composed of PMMA and PS increases with increasing fraction of PS. No measurable change of refractive index of the PMMA films with 4?10 wt.% PS admixture was observed even after 330 h of aging at 363 K, so that in these films no reorientation of PMMA dipoles occurs. Such films are considered as prospective materia

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA5011301" target="_blank" >IAA5011301: Cévní buňky na syntetických polymerech s adhesivními mikrodoménami</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science: Materials in Electronics

ISSN

0957-4522

e-ISSN

—

Svazek periodika

18

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000243397500015

EID výsledku v databázi Scopus

—