Influence of the Yb and Si content on the sintering and phase changes of Yb:YAG laser ceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22310%2F12%3A43894506" target="_blank" >RIV/60461373:22310/12:43894506 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2012.02.045" target="_blank" >http://dx.doi.org/10.1016/j.jeurceramsoc.2012.02.045</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2012.02.045" target="_blank" >10.1016/j.jeurceramsoc.2012.02.045</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of the Yb and Si content on the sintering and phase changes of Yb:YAG laser ceramics

Popis výsledku v původním jazyce

Yb-doped YAG ceramics with Yb concentrations ranging from 0 to 10 at.% were prepared via solid state reaction of oxide powders. Silicon in the form of TEOS was added as a sintering aid in amounts of 0.3 and 0.5 wt.%. Thermal analyses (high-temperature XRD, TG-DSC, dilatometry) were performed on various compositions. Sintering was conducted under high vacuum and clean atmosphere. The influence of TEOS addition and Yb content was observed both in connection with phase changes as a function of temperature,and in relation to the microstructure and properties of the sintered materials.

Název v anglickém jazyce

Influence of the Yb and Si content on the sintering and phase changes of Yb:YAG laser ceramics

Popis výsledku anglicky

Yb-doped YAG ceramics with Yb concentrations ranging from 0 to 10 at.% were prepared via solid state reaction of oxide powders. Silicon in the form of TEOS was added as a sintering aid in amounts of 0.3 and 0.5 wt.%. Thermal analyses (high-temperature XRD, TG-DSC, dilatometry) were performed on various compositions. Sintering was conducted under high vacuum and clean atmosphere. The influence of TEOS addition and Yb content was observed both in connection with phase changes as a function of temperature,and in relation to the microstructure and properties of the sintered materials.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

32

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

BE - Belgické království

Počet stran výsledku

8

Strana od-do

2949-1956

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—