Interfacial design of mixed matrix membranes via grafting pva on UiO-66-NH2 to enhance the gas separation performance

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60461373%3A22340%2F21%3A43922998" target="_blank" >RIV/60461373:22340/21:43922998 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.mdpi.com/2077-0375/11/6/419/htm" target="_blank" >https://www.mdpi.com/2077-0375/11/6/419/htm</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/membranes11060419" target="_blank" >10.3390/membranes11060419</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Interfacial design of mixed matrix membranes via grafting pva on UiO-66-NH2 to enhance the gas separation performance

Popis výsledku v původním jazyce

In this study, defect-free facilitated transport mixed matrix membrane (MMM) with high loading amount of UiO-66-NH2 nanoparticles as metal–organic frameworks (MOFs) was fabricated. The MOFs were covalently bonded with poly (vinyl alcohol) (PVA) to incorporate into a poly (vinyl amine) (PVAm) matrix solution. A uniform UiO-66-NH2 dispersion up to 55 wt.% was observed without precipitation and agglomeration after one month. This can be attributed to the high covalent interaction at interfaces of UiO-66-NH2 and PVAm, which was provided by PVA as a functionalized organic linker. The CO2 permeability and CO2 /N2 and selectivity were significantly enhanced for the fabricated MMM by using optimal fabrication parameters. This improvement in gas performance is due to the strong impact of solubility and decreasing diffusion in obtained dense membrane to promote CO2 transport with a bicarbonate reversible reaction. Therefore, the highest amount of amine functional groups of PVAm among all polymers, plus the abundant amount of amines from UiO-66-NH2, facilitated the preferential CO2 permeation through the bicarbonate reversible reaction between CO2 and –NH2 in humidified conditions. XRD and FTIR were employed to study the MMM chemical structure and polymers–MOF particle interactions. Cross-sectional and surface morphology of the MMM was observed by SEM-EDX and 3D optical profilometer to detect the dispersion of MOFs into the polymer matrix and explore their interfacial morphology. This approach can be extended for a variety of polymer–filler interfacial designs for gas separation applications. © 2021 by the authors. Licensee MDPI, Basel, Switzerland.

Název v anglickém jazyce

Interfacial design of mixed matrix membranes via grafting pva on UiO-66-NH2 to enhance the gas separation performance

Popis výsledku anglicky

In this study, defect-free facilitated transport mixed matrix membrane (MMM) with high loading amount of UiO-66-NH2 nanoparticles as metal–organic frameworks (MOFs) was fabricated. The MOFs were covalently bonded with poly (vinyl alcohol) (PVA) to incorporate into a poly (vinyl amine) (PVAm) matrix solution. A uniform UiO-66-NH2 dispersion up to 55 wt.% was observed without precipitation and agglomeration after one month. This can be attributed to the high covalent interaction at interfaces of UiO-66-NH2 and PVAm, which was provided by PVA as a functionalized organic linker. The CO2 permeability and CO2 /N2 and selectivity were significantly enhanced for the fabricated MMM by using optimal fabrication parameters. This improvement in gas performance is due to the strong impact of solubility and decreasing diffusion in obtained dense membrane to promote CO2 transport with a bicarbonate reversible reaction. Therefore, the highest amount of amine functional groups of PVAm among all polymers, plus the abundant amount of amines from UiO-66-NH2, facilitated the preferential CO2 permeation through the bicarbonate reversible reaction between CO2 and –NH2 in humidified conditions. XRD and FTIR were employed to study the MMM chemical structure and polymers–MOF particle interactions. Cross-sectional and surface morphology of the MMM was observed by SEM-EDX and 3D optical profilometer to detect the dispersion of MOFs into the polymer matrix and explore their interfacial morphology. This approach can be extended for a variety of polymer–filler interfacial designs for gas separation applications. © 2021 by the authors. Licensee MDPI, Basel, Switzerland.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10404 - Polymer science

Projekt

<a href="/cs/project/GA19-14547S" target="_blank" >GA19-14547S: Nové kompozitní membrány pro cílené separace plynů a par (CoMeTS)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Membranes

ISSN

2077-0375

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

12

Strana od-do

419

Kód UT WoS článku

000665996100001

EID výsledku v databázi Scopus

2-s2.0-85108068725