Zr-Based Metal-Organic Framework UiO-66/Ultem® 1000 Membranes for Effective CO2/H2 Separation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F23%3A00574064" target="_blank" >RIV/67985858:_____/23:00574064 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/60461373:22310/23:43928660
Výsledek na webu
<a href="https://hdl.handle.net/11104/0344430" target="_blank" >https://hdl.handle.net/11104/0344430</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/ceat.202200599" target="_blank" >10.1002/ceat.202200599</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Zr-Based Metal-Organic Framework UiO-66/Ultem® 1000 Membranes for Effective CO2/H2 Separation
Popis výsledku v původním jazyce
Mixed-matrix membranes (MMMs) using UiO-66 nanofillers as dispersing inorganic phase and polyetherimide (PEI) as continuous polymeric matrix were synthesized. Different UiO-66 loadings of 10, 20, and 30 wt % were applied. The morphology and UiO-66 dispersion over the prepared MMMs were examined. Gas separation measurements were performed for H2/CO2 gas mixture to evaluate the influence of UiO-66 on the separation yield of resulting membranes. When compared with pristine PEI membranes, MMMs containing metal-organic framework (MOF) nanoparticles revealed superior H2 permeability and H2/CO2 separation factor, e.g., maximum permeability values of 14.6 and 5.5 Barrer were observed for H2 and CO2 at a filler loading of 10 wt % and an applied pressure of 4.0 bar.
Název v anglickém jazyce
Zr-Based Metal-Organic Framework UiO-66/Ultem® 1000 Membranes for Effective CO2/H2 Separation
Popis výsledku anglicky
Mixed-matrix membranes (MMMs) using UiO-66 nanofillers as dispersing inorganic phase and polyetherimide (PEI) as continuous polymeric matrix were synthesized. Different UiO-66 loadings of 10, 20, and 30 wt % were applied. The morphology and UiO-66 dispersion over the prepared MMMs were examined. Gas separation measurements were performed for H2/CO2 gas mixture to evaluate the influence of UiO-66 on the separation yield of resulting membranes. When compared with pristine PEI membranes, MMMs containing metal-organic framework (MOF) nanoparticles revealed superior H2 permeability and H2/CO2 separation factor, e.g., maximum permeability values of 14.6 and 5.5 Barrer were observed for H2 and CO2 at a filler loading of 10 wt % and an applied pressure of 4.0 bar.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
20402 - Chemical process engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF16_026%2F0008413" target="_blank" >EF16_026/0008413: Strategické partnerství pro environmentální technologie a produkci energie</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Chemical Engineering & Technology
ISSN
0930-7516
e-ISSN
1521-4125
Svazek periodika
46
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
2046-2053
Kód UT WoS článku
001016104300001
EID výsledku v databázi Scopus
2-s2.0-85162731974