A method for electrochemical growth of homogeneous nanocrystalline ZnO thin films at room temperature

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F09%3A00329255" target="_blank" >RIV/61388955:_____/09:00329255 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A method for electrochemical growth of homogeneous nanocrystalline ZnO thin films at room temperature

Popis výsledku v původním jazyce

We report the electrodeposition at room temperature (25 °C), in a potentiostatic mode, of cohesive nanocrystalline ZnO thin films from an oxygenated zinc chloride bath. It is shown that the bath saturation by molecular oxygen precursor is a key parameterto grow the oxide at low temperature. After low O2 bubbling the solution is not saturated and the surface is more or less passivated by an amorphous Zn(OH)2 veil-like thin layer. After intense and long molecular oxygen bubbling, the current density rapidly increases after an induction period of about 800 s. At the foot of the current onset, crystallized ZnO seeds appear entrapped in the initial amorphous layer. The film nucleation is a delayed process. The electrode is subsequently covered by a homogeneous ZnO film with structures of several hundreds of nanometers in length composed of nanocrystals with size of about 17 nm.

Název v anglickém jazyce

A method for electrochemical growth of homogeneous nanocrystalline ZnO thin films at room temperature

Popis výsledku anglicky

We report the electrodeposition at room temperature (25 °C), in a potentiostatic mode, of cohesive nanocrystalline ZnO thin films from an oxygenated zinc chloride bath. It is shown that the bath saturation by molecular oxygen precursor is a key parameterto grow the oxide at low temperature. After low O2 bubbling the solution is not saturated and the surface is more or less passivated by an amorphous Zn(OH)2 veil-like thin layer. After intense and long molecular oxygen bubbling, the current density rapidly increases after an induction period of about 800 s. At the foot of the current onset, crystallized ZnO seeds appear entrapped in the initial amorphous layer. The film nucleation is a delayed process. The electrode is subsequently covered by a homogeneous ZnO film with structures of several hundreds of nanometers in length composed of nanocrystals with size of about 17 nm.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA400400909" target="_blank" >IAA400400909: Membrány na bázi zeolitů pro membránové reaktory pro konverzi oxidu uhelnatého vodní parou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Electrochimica acta

ISSN

0013-4686

e-ISSN

—

Svazek periodika

54

Číslo periodika v rámci svazku

28

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000271151600060

EID výsledku v databázi Scopus

—