Thermal behaviour of the precursors of ruthenia-titania based mixed oxides

Popis výsledku v původním jazyce

Studies on ruthenia-titania based materials have been attractive because of their catalytic properties as well as due to the possibility of solid solution formation. Samples of pure ruthenia and ruthenia containing various amounts of titania (10-70 mol%)were investigated during heating of their hydroxide precursors from 20 to 800 degrees C in air using emanation thermal analysis (ETA), thermogravimetry (TG), and differential thermal analysis (DTA). The resulting mixed oxide type materials were characterized by X-ray diffraction (XRD), which indicate the presence of three ruthenia-titania phases. The onset temperature of the crystallization of materials was identified by ETA results, whereas DTA effects characterized the crystallization in bulk of thesamples. A good agreement was found between the ETA results and other characterization techniques used.

Název v anglickém jazyce

Thermal behaviour of the precursors of ruthenia-titania based mixed oxides

Popis výsledku anglicky

Studies on ruthenia-titania based materials have been attractive because of their catalytic properties as well as due to the possibility of solid solution formation. Samples of pure ruthenia and ruthenia containing various amounts of titania (10-70 mol%)were investigated during heating of their hydroxide precursors from 20 to 800 degrees C in air using emanation thermal analysis (ETA), thermogravimetry (TG), and differential thermal analysis (DTA). The resulting mixed oxide type materials were characterized by X-ray diffraction (XRD), which indicate the presence of three ruthenia-titania phases. The onset temperature of the crystallization of materials was identified by ETA results, whereas DTA effects characterized the crystallization in bulk of thesamples. A good agreement was found between the ETA results and other characterization techniques used.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Thermal Analysis and Calorimetry: an international forum for thermal studies

ISSN

1388-6150

e-ISSN

—

Svazek periodika

80

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

HU - Maďarsko

Počet stran výsledku

7

Strana od-do

671-677

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—