Size effects in MD simulations of fracture in bcc iron crystals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388998%3A_____%2F23%3A00579592" target="_blank" >RIV/61388998:_____/23:00579592 - isvavai.cz</a>

Výsledek na webu

<a href="https://iopscience.iop.org/article/10.1088/1402-4896/ad0d67" target="_blank" >https://iopscience.iop.org/article/10.1088/1402-4896/ad0d67</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1402-4896/ad0d67" target="_blank" >10.1088/1402-4896/ad0d67</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Size effects in MD simulations of fracture in bcc iron crystals

Popis výsledku v původním jazyce

3D parallel simulations via molecular dynamics (MD) show that the brittle or ductile behavior of the atomistic samples with the edge crack (001)[110] (crack plane/crack front) depends on size of the sample. For all samples tested, the crack initiation is brittle. However, the subsequent crack growth can be inhibited by twin formation, crack deflections and new dislocation emissions on {123} slip planes and the final fracture can also be then ductile, which depends mainly on thickness B of the atomistic sample. MD results comply with the stress analysis performed by the anisotropic linear fracture mechanics and with some experimental observations.

Název v anglickém jazyce

Size effects in MD simulations of fracture in bcc iron crystals

Popis výsledku anglicky

3D parallel simulations via molecular dynamics (MD) show that the brittle or ductile behavior of the atomistic samples with the edge crack (001)[110] (crack plane/crack front) depends on size of the sample. For all samples tested, the crack initiation is brittle. However, the subsequent crack growth can be inhibited by twin formation, crack deflections and new dislocation emissions on {123} slip planes and the final fracture can also be then ductile, which depends mainly on thickness B of the atomistic sample. MD results comply with the stress analysis performed by the anisotropic linear fracture mechanics and with some experimental observations.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA23-05338S" target="_blank" >GA23-05338S: Mechanické a strukturní vlastnosti 3D tištěné slitiny AlSi10Mg v závislosti na míře recyklace prášku</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica Scripta

ISSN

0031-8949

e-ISSN

1402-4896

Svazek periodika

98

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

22

Strana od-do

125974

Kód UT WoS článku

001109685800001

EID výsledku v databázi Scopus

2-s2.0-85178567407