Coloring of radiation damages in ion-implanted poly(aryl ether ether ketone): LiCl uptake and thermal desorption.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F02%3A49020016" target="_blank" >RIV/61389005:_____/02:49020016 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Coloring of radiation damages in ion-implanted poly(aryl ether ether ketone): LiCl uptake and thermal desorption.

Popis výsledku v původním jazyce

Poly(aryl ether ether ketone) (PEEK) films irradiated with 2 MeV O+ and Ar+ ions to fluences in the range 10(11)-10(13) cm(-2) were treated with 5 mol/L LiCl aqueous solution at 100degreesC for 1 h. After removal of excessive, weakly bound LiCl the samples were annealed at temperatures from 50 to 250degreesC for 1 h to check the mobility of the incorporated LiCl. The amount of incorporated LiCl and its depth profile were determined using the neutron depth-profiling (NDP) technique, which makes use of the Li-6(n(th), He-4) H-3 nuclear reaction. Up to the maximum annealing temperature no significant escape of the LiCl was observed. With increasing annealing temperature, a gradual migration of LiCl dopant toward the sample surface was observed on the irradiated PEEK samples.

Název v anglickém jazyce

Coloring of radiation damages in ion-implanted poly(aryl ether ether ketone): LiCl uptake and thermal desorption.

Popis výsledku anglicky

Poly(aryl ether ether ketone) (PEEK) films irradiated with 2 MeV O+ and Ar+ ions to fluences in the range 10(11)-10(13) cm(-2) were treated with 5 mol/L LiCl aqueous solution at 100degreesC for 1 h. After removal of excessive, weakly bound LiCl the samples were annealed at temperatures from 50 to 250degreesC for 1 h to check the mobility of the incorporated LiCl. The amount of incorporated LiCl and its depth profile were determined using the neutron depth-profiling (NDP) technique, which makes use of the Li-6(n(th), He-4) H-3 nuclear reaction. Up to the maximum annealing temperature no significant escape of the LiCl was observed. With increasing annealing temperature, a gradual migration of LiCl dopant toward the sample surface was observed on the irradiated PEEK samples.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BG - Jaderná, atomová a molekulová fyzika, urychlovače

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Applied Polymer Science

ISSN

0021-8995

e-ISSN

—

Svazek periodika

83

Číslo periodika v rámci svazku

N/A

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

2780-2784

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—