Study of water uptake in poly(ether ether ketone) irradiated by MeV O+ and Au+ ions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F20%3A00523922" target="_blank" >RIV/61389005:_____/20:00523922 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1080/10420150.2019.1701463" target="_blank" >https://doi.org/10.1080/10420150.2019.1701463</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1080/10420150.2019.1701463" target="_blank" >10.1080/10420150.2019.1701463</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Study of water uptake in poly(ether ether ketone) irradiated by MeV O+ and Au+ ions

Popis výsledku v původním jazyce

Poly(ether ether ketone) (PEEK) was irradiated with 4 MeV O+ and 5 and 10 MeV Au+ ions to the fluences from 10(12) to 10(14 )cm(-2) and then treated in 5 M/l water solution of LiCl for one month at room temperature. After drying and removal of LiCl surface contamination, the depth distribution of LiCl embeded in PEEK was measured by the neutron depth profilig method (NDP) sensitive to Li-6 isotope. Embeded LiCl is believed to map distribution of water diffusing into PEEK interior. The results show that the PEEK irradiated to the fluences above 1.10(13)cm(-2) is prone to water penetration to the depths of few microns. On the pristine PEEK and that irradiated to lower ion fluences only a surface Li contamination is observed.

Název v anglickém jazyce

Study of water uptake in poly(ether ether ketone) irradiated by MeV O+ and Au+ ions

Popis výsledku anglicky

Poly(ether ether ketone) (PEEK) was irradiated with 4 MeV O+ and 5 and 10 MeV Au+ ions to the fluences from 10(12) to 10(14 )cm(-2) and then treated in 5 M/l water solution of LiCl for one month at room temperature. After drying and removal of LiCl surface contamination, the depth distribution of LiCl embeded in PEEK was measured by the neutron depth profilig method (NDP) sensitive to Li-6 isotope. Embeded LiCl is believed to map distribution of water diffusing into PEEK interior. The results show that the PEEK irradiated to the fluences above 1.10(13)cm(-2) is prone to water penetration to the depths of few microns. On the pristine PEEK and that irradiated to lower ion fluences only a surface Li contamination is observed.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Radiation Effects and Defects in Solids

ISSN

1042-0150

e-ISSN

—

Svazek periodika

175

Číslo periodika v rámci svazku

3-4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

318-324

Kód UT WoS článku

000522130000009

EID výsledku v databázi Scopus

2-s2.0-85082604869