Popis výsledku v původním jazyce
Poly(ether ether ketone) was irradiated with 3.0 MeV Si2+, 3.25 MeV CU2+ and 4.8 MeV Ag2+ ions to the fluences from 10(12) to 10(14) cm(-2) and the effects of irradiation were studied using ERDA, RBS and FTIR methods. The irradiation leads to release ofhydrogen from the PEEK surface layer modified by the ion beam. The release is mild for low ion fluences but it becomes more pronounced at the ion fluences above 10(13) cm(-2). At highest ion fluences the hydrogen concentration falls to 20-35% of its initial value. In contrast to hydrogen no significant oxygen release was observed. The kinetic of the hydrogen release is similar for the three ion species. FTIR measurement shows deep structural changes of the polymer structure resulting from the ion irradiation.
Název v anglickém jazyce
Modification of poly(ether ether ketone) by ion irradiation
Popis výsledku anglicky
Poly(ether ether ketone) was irradiated with 3.0 MeV Si2+, 3.25 MeV CU2+ and 4.8 MeV Ag2+ ions to the fluences from 10(12) to 10(14) cm(-2) and the effects of irradiation were studied using ERDA, RBS and FTIR methods. The irradiation leads to release ofhydrogen from the PEEK surface layer modified by the ion beam. The release is mild for low ion fluences but it becomes more pronounced at the ion fluences above 10(13) cm(-2). At highest ion fluences the hydrogen concentration falls to 20-35% of its initial value. In contrast to hydrogen no significant oxygen release was observed. The kinetic of the hydrogen release is similar for the three ion species. FTIR measurement shows deep structural changes of the polymer structure resulting from the ion irradiation.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BG - Jaderná, atomová a molekulová fyzika, urychlovače
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Nuclear Instruments & Methods in Physics Research Section B
ISSN
0168-583X
e-ISSN
—
Svazek periodika
266
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
—
Kód UT WoS článku
000253517400012
EID výsledku v databázi Scopus
—