Izotermická oxidace kovových povlaků nanesených pomocí plazmového hořáku stabilizovaného vodou

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F06%3A00040304" target="_blank" >RIV/61389021:_____/06:00040304 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Isothermal oxidation of metallic coatings deposited by a water-stabilized plasma gun

Popis výsledku v původním jazyce

Plasma deposits of two high-alloy steels, nickel and a Ni-Cr alloy were studied from the point of view of their isothermal oxidation at elevated temperatures. Deposits separated from the substrate were measured by a gravimetric method after oxidation at1000-1150 K for various periods of time up to 144 hours. The oxidation rate was approximately parabolic. The oxide layers growing on all alloys contained very low amounts of Cr. This is in a strong contrast to the oxides resulting from plasma spraying, which are significantly enriched in Cr as compared to the alloy composition. The preferential oxidation of Cr during plasma spraying results in Cr depletion, which is the main reason for rapid oxidation of steel deposits during isothermal oxidation tests.The plasma deposits of nickel and the Ni-Cr alloy exhibited significantly better oxidation resistance.

Název v anglickém jazyce

Isothermal oxidation of metallic coatings deposited by a water-stabilized plasma gun

Popis výsledku anglicky

Plasma deposits of two high-alloy steels, nickel and a Ni-Cr alloy were studied from the point of view of their isothermal oxidation at elevated temperatures. Deposits separated from the substrate were measured by a gravimetric method after oxidation at1000-1150 K for various periods of time up to 144 hours. The oxidation rate was approximately parabolic. The oxide layers growing on all alloys contained very low amounts of Cr. This is in a strong contrast to the oxides resulting from plasma spraying, which are significantly enriched in Cr as compared to the alloy composition. The preferential oxidation of Cr during plasma spraying results in Cr depletion, which is the main reason for rapid oxidation of steel deposits during isothermal oxidation tests.The plasma deposits of nickel and the Ni-Cr alloy exhibited significantly better oxidation resistance.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0710" target="_blank" >GA106/03/0710: Změny složení keramických a kovových materiálů při jejich plazmovém stříkání</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

44

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

8

Strana od-do

41-48

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—