High Temperature Oxidation of Thermally Sprayed Coatings

Popis výsledku v původním jazyce

This work described high temperature isothermal oxidation of plasma sprayed coatings. For spraying were applied four materials: steel ČSN 17 350 approximately to AISI 316, ČSN 17 021 approximately to AISI 410, unalloyed nickel and NiCr alloy (Ni 80%, Cr20%). Into the experiment were inserted two smelting products into the experiment to compare results of high temperature isothermal oxidation of thermally sprayed coatings: AISI 316 and unalloyed nickel. Grain size of powders was at range of 100 up to 140 mm. The spraying distance (plasma gun nozzle - substrate surface) was 400 mm. A 160 kW water - stabilized plasma gun WPS PAL160 was used for the spraying. As a substrate we used low carbon steel ČSN 11 373 format 100 x 20 x 5 mm. After separation of plasma coatings the thickness of separated coatings did about 1,5 mm and their surface was from 6 to 9 cm2.

Název v anglickém jazyce

High Temperature Oxidation of Thermally Sprayed Coatings

Popis výsledku anglicky

This work described high temperature isothermal oxidation of plasma sprayed coatings. For spraying were applied four materials: steel ČSN 17 350 approximately to AISI 316, ČSN 17 021 approximately to AISI 410, unalloyed nickel and NiCr alloy (Ni 80%, Cr20%). Into the experiment were inserted two smelting products into the experiment to compare results of high temperature isothermal oxidation of thermally sprayed coatings: AISI 316 and unalloyed nickel. Grain size of powders was at range of 100 up to 140 mm. The spraying distance (plasma gun nozzle - substrate surface) was 400 mm. A 160 kW water - stabilized plasma gun WPS PAL160 was used for the spraying. As a substrate we used low carbon steel ČSN 11 373 format 100 x 20 x 5 mm. After separation of plasma coatings the thickness of separated coatings did about 1,5 mm and their surface was from 6 to 9 cm2.

Druh

A - Audiovizuální tvorba

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

ISBN

80-01-02708-2

Místo vydání

Praha

Název nakladatele resp. objednatele

—

Verze

—

Identifikační číslo nosiče

neuvedeno