CHOSEN METALLOGRAPHIC AND MICROFRACTOGRAPHIC PARAMETERS OF EXPLOSIVELY WEALDED BIMETAL 304 SS AND TI.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F11%3A86079879" target="_blank" >RIV/61989100:27230/11:86079879 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/11:86079879

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

CHOSEN METALLOGRAPHIC AND MICROFRACTOGRAPHIC PARAMETERS OF EXPLOSIVELY WEALDED BIMETAL 304 SS AND TI.

Popis výsledku v původním jazyce

The work deals with evaluation of bimetal joint of steel 304SS and commercially pure Ti after explosive welding and next annealing (600°C/1.5 hours/air) with aim to refine the grains of Ti-matrix. Bonding line shows sinusoidal character with noticeable curls in crest unlike the trough of the sine curve. The heat treatment does not change its character. Work demonstrates evaluated chosen metallographic parameters of the joint and its close neighbouring as e.g. wave length, amplitude, thickness of bondingline and parameter of grains compressed thickness between crest and trough, concentrates on analysis of intermetallic particles in the bonding line or in vicinity of joint and micro-fractographic response of joint fracture surfaces after tensile tests.Fracture surfaces shows mixture of both welded matrixes with dominant Ti part and/or practically balanced Ti-Fe portion. Results are confronted with accessible literature pieces of information.

Název v anglickém jazyce

CHOSEN METALLOGRAPHIC AND MICROFRACTOGRAPHIC PARAMETERS OF EXPLOSIVELY WEALDED BIMETAL 304 SS AND TI.

Popis výsledku anglicky

The work deals with evaluation of bimetal joint of steel 304SS and commercially pure Ti after explosive welding and next annealing (600°C/1.5 hours/air) with aim to refine the grains of Ti-matrix. Bonding line shows sinusoidal character with noticeable curls in crest unlike the trough of the sine curve. The heat treatment does not change its character. Work demonstrates evaluated chosen metallographic parameters of the joint and its close neighbouring as e.g. wave length, amplitude, thickness of bondingline and parameter of grains compressed thickness between crest and trough, concentrates on analysis of intermetallic particles in the bonding line or in vicinity of joint and micro-fractographic response of joint fracture surfaces after tensile tests.Fracture surfaces shows mixture of both welded matrixes with dominant Ti part and/or practically balanced Ti-Fe portion. Results are confronted with accessible literature pieces of information.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

20th Anniversary International Conference on Metallurgy and Materials: METAL 2011

ISBN

978-80-87294-24-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

543-548

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

18. 5. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—