Drop Evaporation Test for stress corrosion cracking study

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F03%3A00008728" target="_blank" >RIV/61989100:27360/03:00008728 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Drop Evaporation Test for stress corrosion cracking study

Popis výsledku v původním jazyce

The drop evaporation test (DET) was developed for study of stainless steels resistance to stress corrosion cracking (SCC) at elevated temperatures 120 - 300 °C under constant external load and dropping of diluted sodium chloride water solution. The resistance to SCC is determined according to time to fracture - tensile stress relations and conventional threshold stress. The alloy (steel) NiCrWTiAl 35-15-5 after thermal hardening and long-time service exposition was tested under DET conditions and corrosion cracks were evaluated by metallography and fractography. The microscopic pits and corrosion crack tips coordinates measurement by the travelling microscope method allowed to determine their lengths and rates as function of time and stress intensity factor. These calculated rates were higher when cracks leaving the pits. The resistance to intergranular corrosion was compared by DL-EPR (double loop electrochemical potenciokinetic reactivation) method.

Název v anglickém jazyce

Drop Evaporation Test for stress corrosion cracking study

Popis výsledku anglicky

The drop evaporation test (DET) was developed for study of stainless steels resistance to stress corrosion cracking (SCC) at elevated temperatures 120 - 300 °C under constant external load and dropping of diluted sodium chloride water solution. The resistance to SCC is determined according to time to fracture - tensile stress relations and conventional threshold stress. The alloy (steel) NiCrWTiAl 35-15-5 after thermal hardening and long-time service exposition was tested under DET conditions and corrosion cracks were evaluated by metallography and fractography. The microscopic pits and corrosion crack tips coordinates measurement by the travelling microscope method allowed to determine their lengths and rates as function of time and stress intensity factor. These calculated rates were higher when cracks leaving the pits. The resistance to intergranular corrosion was compared by DL-EPR (double loop electrochemical potenciokinetic reactivation) method.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F1569" target="_blank" >GA106/02/1569: Studium degradace korozivzdorných materiálů v podmínkách vysolování za zvýšených teplot</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

The Europ. Cor. Congress EUROCORR 2003

ISBN

80-81-365

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

25-33

Název nakladatele

Eurocorr

Místo vydání

Budapest

Místo konání akce

Terchova

Datum konání akce

28. 10. 2003

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—