Studium iniciace korozního praskání vysokolegovaných slitin

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F04%3A00010091" target="_blank" >RIV/61989100:27360/04:00010091 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Study of stress corrosion cracking initiation of high alloy materials

Popis výsledku v původním jazyce

In the contribution is studied the initiation and propagation of stress corrosion cracking of high alloy materials. The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, SCC, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 200 - 300 °C underconstant external load using a chloride containing water solution. The initiation and propagation of short cracks as well as pits were observed during the test. The crack initiation and/or propagation can be influenced by cyclic thermal stresses, when the diluted NaCl water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derrive the crack growth lengths and rates of sho

Název v anglickém jazyce

Study of stress corrosion cracking initiation of high alloy materials

Popis výsledku anglicky

In the contribution is studied the initiation and propagation of stress corrosion cracking of high alloy materials. The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, SCC, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 200 - 300 °C underconstant external load using a chloride containing water solution. The initiation and propagation of short cracks as well as pits were observed during the test. The crack initiation and/or propagation can be influenced by cyclic thermal stresses, when the diluted NaCl water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derrive the crack growth lengths and rates of sho

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F1569" target="_blank" >GA106/02/1569: Studium degradace korozivzdorných materiálů v podmínkách vysolování za zvýšených teplot</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Pros.of Conf. EUROCORR 2004, Nice, France,

ISBN

6048-5014

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

81-86

Název nakladatele

EFC Paříž

Místo vydání

Paříž

Místo konání akce

Nice, Francie

Datum konání akce

12. 9. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—