Matematické modelování korozního praskání během zkoušky DET
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00013240" target="_blank" >RIV/61989100:27360/05:00013240 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68145535:_____/05:00027388
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study and computer modelling of stress corrosion cracking during DET test
Popis výsledku v původním jazyce
The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test(DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 °C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test by the travelling microscope method. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. We attend to model stress changes in the testing specimens induced by cooling the heated sample by failing water solution drops. The modeling uses finite element analysis of formulated thermoelasticity problem.
Název v anglickém jazyce
Study and computer modelling of stress corrosion cracking during DET test
Popis výsledku anglicky
The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test(DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 °C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test by the travelling microscope method. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. We attend to model stress changes in the testing specimens induced by cooling the heated sample by failing water solution drops. The modeling uses finite element analysis of formulated thermoelasticity problem.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F03%2F0039" target="_blank" >GA106/03/0039: Posouzení odolnosti stabilizovaných a nestabilizovaných austenitických ocelí ke koroznímu praskání za zvýšených teplot a tlaků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2005
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Sborník vědeckých prací VŠB-TU Ostrava, řada hutnická
ISSN
0474-8484
e-ISSN
—
Svazek periodika
48
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
7
Strana od-do
9-15
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—