COMPUTER MODELING OF STRESS CORROSION CRACKING DURING DROP EVAPORATION TEST (DET)

Popis výsledku v původním jazyce

The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion in passive state (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The DropEvaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 °C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test by the travelling microscope method. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. We attend to model stress changes in the testing specimens induced by cooling the heated sample by failing water solution drops. The modeling uses finite element analysis of formulated thermoelasticity problem.

Název v anglickém jazyce

COMPUTER MODELING OF STRESS CORROSION CRACKING DURING DROP EVAPORATION TEST (DET)

Popis výsledku anglicky

The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion in passive state (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The DropEvaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 °C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test by the travelling microscope method. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. We attend to model stress changes in the testing specimens induced by cooling the heated sample by failing water solution drops. The modeling uses finite element analysis of formulated thermoelasticity problem.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F1621" target="_blank" >GA106/06/1621: Korozní odolnost pasivního stavu vysokolegovaných materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

1st International Conference Corrosion and Material Protection EFC (10th Conference AKI 2007)

ISBN

978-80-903933-0-1

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

83-89

Název nakladatele

SVÚOM, Praha

Místo vydání

Praha

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—