Stress corrosion cracking evaluation of high alloy steel (X2CrNiMoN 22-5-3) by DET

Popis výsledku v původním jazyce

In the paper is studied the initiation and propagation of stress corrosion cracking of high alloy materials. The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, SCC, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC). The initiation and propagation of short cracks aswell as pits were observed during the test. The crack initiation and/or propagation can be influenced by cyclic thermal stresses, when the diluted NaCl water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derrive the crack growth lengths and rates of short and/or small cracks.

Název v anglickém jazyce

Stress corrosion cracking evaluation of high alloy steel (X2CrNiMoN 22-5-3) by DET

Popis výsledku anglicky

In the paper is studied the initiation and propagation of stress corrosion cracking of high alloy materials. The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, SCC, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC). The initiation and propagation of short cracks aswell as pits were observed during the test. The crack initiation and/or propagation can be influenced by cyclic thermal stresses, when the diluted NaCl water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derrive the crack growth lengths and rates of short and/or small cracks.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F1569" target="_blank" >GA106/02/1569: Studium degradace korozivzdorných materiálů v podmínkách vysolování za zvýšených teplot</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Mechanika Zeszyty Naukowe

ISSN

1429-6055

e-ISSN

—

Svazek periodika

298

Číslo periodika v rámci svazku

298

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

17-22

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—