Úloha Al2O3 v semi-metalických frikčních materiálech a jeho vliv na účinost

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F08%3A00019843" target="_blank" >RIV/61989100:27640/08:00019843 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Role of Al2O3 in semi-metallic friction materials and its effects on friction and wear performance

Popis výsledku v původním jazyce

In this work the semi-metallic friction composites with moderately increased content of Al2O3 (0, 3.4, 5.6, 9.0, and 14.6 vol%) were successfully fabricated by casting technology and their tribological properties were evaluated. The character of frictionsurfaces was confirmed by SEM. The sample with 5.6 vol% of Al2O3 offers the best tribological property among the prepared formulations, and is characterized by high and steady friction coefficient (about 0.45) and low wear. With the temperature increasing, the stibnite patches population on friction surface increases and individual steel fibers spread due to their plastic deformation to form larger primary contact plateaus. The area covered by contact primary plateaus decreases with the alumina contentincreasing.

Název v anglickém jazyce

Role of Al2O3 in semi-metallic friction materials and its effects on friction and wear performance

Popis výsledku anglicky

In this work the semi-metallic friction composites with moderately increased content of Al2O3 (0, 3.4, 5.6, 9.0, and 14.6 vol%) were successfully fabricated by casting technology and their tribological properties were evaluated. The character of frictionsurfaces was confirmed by SEM. The sample with 5.6 vol% of Al2O3 offers the best tribological property among the prepared formulations, and is characterized by high and steady friction coefficient (about 0.45) and low wear. With the temperature increasing, the stibnite patches population on friction surface increases and individual steel fibers spread due to their plastic deformation to form larger primary contact plateaus. The area covered by contact primary plateaus decreases with the alumina contentincreasing.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/1P05ME741" target="_blank" >1P05ME741: Optimalizace složení a vlastností frikčních kompozitních materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Tribology Transactions

ISSN

0301-6978

e-ISSN

—

Svazek periodika

6

Číslo periodika v rámci svazku

51

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—