From Shelled Ge Nanowires to SiC Nanotubes

Popis výsledku v původním jazyce

Shelled germanium nanowires up to 100 nm in diameter and several micrometers in length were prepared by low pressure chemical vapor deposition (LPCVD) of tris(trimethylsilyl)germane (SiMe3)3GeH. Vapors of the precursor were deposited on tantalum substrates in an oven at 365 °C. Subsequently, the products were annealed at 700 °C in vacuum. The wires consist of a crystalline Ge core surrounded by a two-layer jacket. The presence of hexagonal Ge in the core was documented in some of the nanowires. The inner jacket is formed by amorphous germanium, the outer part by an Si/C material. By annealing at 900 °C, germanium in the core is expelled and nanotubes formed by the Si/C material remain. The samples were studied by SEM, HRTEM, EDX, FTIR and Raman spectroscopy, and the XRD technique.

Název v anglickém jazyce

From Shelled Ge Nanowires to SiC Nanotubes

Popis výsledku anglicky

Shelled germanium nanowires up to 100 nm in diameter and several micrometers in length were prepared by low pressure chemical vapor deposition (LPCVD) of tris(trimethylsilyl)germane (SiMe3)3GeH. Vapors of the precursor were deposited on tantalum substrates in an oven at 365 °C. Subsequently, the products were annealed at 700 °C in vacuum. The wires consist of a crystalline Ge core surrounded by a two-layer jacket. The presence of hexagonal Ge in the core was documented in some of the nanowires. The inner jacket is formed by amorphous germanium, the outer part by an Si/C material. By annealing at 900 °C, germanium in the core is expelled and nanotubes formed by the Si/C material remain. The samples were studied by SEM, HRTEM, EDX, FTIR and Raman spectroscopy, and the XRD technique.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nanotechnology

ISSN

0957-4484

e-ISSN

—

Svazek periodika

20

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

261795500015

EID výsledku v databázi Scopus

—