Creep in ODS copper reinforced with alumina short fibres - DRS copper.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F03%3A07033037" target="_blank" >RIV/68081723:_____/03:07033037 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep in ODS copper reinforced with alumina short fibres - DRS copper.

Popis výsledku v původním jazyce

Creep in copper dispersion strengthened with fine alumina particles (oxide dispersion strengthened (ODS) Cu) and reinforced with alumina short fibresůůa DRS Cu compositeůůis investigated in two temperature intervals, namely 673ů773 K, lower temperature interval (LTI) and 923ů1023 K, higher temperature interval (HTI). It is shown that in both intervals creep is associated with true threshold stresses decreasing with increasing temperature more strongly than the shear modulus of copper. The true thresholdstress in the composite is higher than that in the composite matrix (i.e. ODS copper) by a factor , by which the flow stress in the matrix is reduced due to load transfer. The minimum creep strain rate is found to be dislocation core diffusion controlled in LTI and lattice diffusion controlled in HTI. High values of the apparent activation energies are fully explained in terms of the temperature dependence of the true threshold stress in LTI as well as in HTI. Also the values of the app

Název v anglickém jazyce

Creep in ODS copper reinforced with alumina short fibres - DRS copper.

Popis výsledku anglicky

Creep in copper dispersion strengthened with fine alumina particles (oxide dispersion strengthened (ODS) Cu) and reinforced with alumina short fibresůůa DRS Cu compositeůůis investigated in two temperature intervals, namely 673ů773 K, lower temperature interval (LTI) and 923ů1023 K, higher temperature interval (HTI). It is shown that in both intervals creep is associated with true threshold stresses decreasing with increasing temperature more strongly than the shear modulus of copper. The true thresholdstress in the composite is higher than that in the composite matrix (i.e. ODS copper) by a factor , by which the flow stress in the matrix is reduced due to load transfer. The minimum creep strain rate is found to be dislocation core diffusion controlled in LTI and lattice diffusion controlled in HTI. High values of the apparent activation energies are fully explained in terms of the temperature dependence of the true threshold stress in LTI as well as in HTI. Also the values of the app

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/IBS2041001" target="_blank" >IBS2041001: Degradace vlastností a životnost inženýrských materiálů při jejich mechanickém namáhání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Material Science and Engineering A. A

ISSN

0921-5093

e-ISSN

—

Svazek periodika

355

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

267-276

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—