Creep disperzně zpevněné mědi vyztužené krátkými wolframovými vlákny - matrice měď ODS/kompozit s krátkými wolframovými vlákny

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108189" target="_blank" >RIV/68081723:_____/04:00108189 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep in ODS copper reinforced with tungsten short fibres - an ODS copper-matrix/tungsten-short fibre composite

Popis výsledku v původním jazyce

Creep in copper dispersion-strengthened with fine alumina particles and reinforced with tungsten short fibres is investigated at three temperatures ranging from 923 to 1023 K. It is shown that creep is associated with a true threshold stress decreasing with increasing temperature more strongly than the shear modulus of copper. The true threshold stress in the composite is higher than that in the composite matrix by a factor A, by which the flow stress in the matrix is reduced due to the load transfer. The minimum creep strain rate is found to be lattice diffusion controlled and to depend on the fifth power of applied stress. The values of the apparent activation energy of creep are higher than that of the activation enthalpy of lattice self-diffusion in the composite matrix, which is fully explained in terms of the temperature dependence of the true threshold stress

Název v anglickém jazyce

Creep in ODS copper reinforced with tungsten short fibres - an ODS copper-matrix/tungsten-short fibre composite

Popis výsledku anglicky

Creep in copper dispersion-strengthened with fine alumina particles and reinforced with tungsten short fibres is investigated at three temperatures ranging from 923 to 1023 K. It is shown that creep is associated with a true threshold stress decreasing with increasing temperature more strongly than the shear modulus of copper. The true threshold stress in the composite is higher than that in the composite matrix by a factor A, by which the flow stress in the matrix is reduced due to the load transfer. The minimum creep strain rate is found to be lattice diffusion controlled and to depend on the fifth power of applied stress. The values of the apparent activation energy of creep are higher than that of the activation enthalpy of lattice self-diffusion in the composite matrix, which is fully explained in terms of the temperature dependence of the true threshold stress

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/IBS2041001" target="_blank" >IBS2041001: Degradace vlastností a životnost inženýrských materiálů při jejich mechanickém namáhání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Zeitschrift fur Metallkunde

ISSN

0044-3093

e-ISSN

—

Svazek periodika

95

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

6

Strana od-do

179-184

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—