Creep mědi disperzně zpevněné jemnými částicemi a vyztužené krátkými vlákny oxidu hliníku v měděné matrici ODS

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F04%3A00108210" target="_blank" >RIV/68081723:_____/04:00108210 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres-in ODS copper matrix..

Popis výsledku v původním jazyce

Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres is investigated in two temperature intervals, namely lower temperature interval (LTI) 673-773 K and higher temperature interval (HTI) 923-1023 K.In both intervals, creep is associated with true threshold stresses decreasing with increasing temperature more strongly than the shear modulus of copper. The true threshold stress in the composite is higher than that in its matrix by a factor 2, by which the flow stress in the matrix is reduced due to load transfer. The creep strain rate is dislocation core diffusion controlled in LTI and lattice diffusion controlled in HTI. High values of the activation energies are explained in terms of the temperature dependence of the true threshold stress in LTI as well as in HTI. The high values of the stress exponents are explained in terms of the true threshold stresses. The true threshold stress is identified with the detachment stress

Název v anglickém jazyce

Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres-in ODS copper matrix..

Popis výsledku anglicky

Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres is investigated in two temperature intervals, namely lower temperature interval (LTI) 673-773 K and higher temperature interval (HTI) 923-1023 K.In both intervals, creep is associated with true threshold stresses decreasing with increasing temperature more strongly than the shear modulus of copper. The true threshold stress in the composite is higher than that in its matrix by a factor 2, by which the flow stress in the matrix is reduced due to load transfer. The creep strain rate is dislocation core diffusion controlled in LTI and lattice diffusion controlled in HTI. High values of the activation energies are explained in terms of the temperature dependence of the true threshold stress in LTI as well as in HTI. The high values of the stress exponents are explained in terms of the true threshold stresses. The true threshold stress is identified with the detachment stress

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/IBS2041001" target="_blank" >IBS2041001: Degradace vlastností a životnost inženýrských materiálů při jejich mechanickém namáhání</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Alloys and Compounds

ISSN

0925-8388

e-ISSN

—

Svazek periodika

378

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

123-126

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—