Iron and molybdenum diffusion in Fe76Mo8B15Cu1 alloy

Popis výsledku v původním jazyce

Fe and Mo tracer diffusion in Fe76Mo8B15Cu1 alloy was studied using serial sectioning method in the temperature range 527 ? 649 K. The ribbon-like samples were annealed at 695 K for 1 and 5 hours before the diffusion experiments; the volume fraction of crystalline phase was checked by the Mössbauer spectroscopy. Concentration profiles obtained by sputtering by Ar+ ions in a glow discharge show two distinct branches suggesting that two diffusion paths are operating. Arrhenius plot of measured diffusion coefficients was not linear in the whole temperature studied interval, which may be due to predominance of less energetically demanding jumps at lower temperatures and higher effective activation enthalpy at higher temperatures. The kink temperature was about 630 K.

Název v anglickém jazyce

Iron and molybdenum diffusion in Fe76Mo8B15Cu1 alloy

Popis výsledku anglicky

Fe and Mo tracer diffusion in Fe76Mo8B15Cu1 alloy was studied using serial sectioning method in the temperature range 527 ? 649 K. The ribbon-like samples were annealed at 695 K for 1 and 5 hours before the diffusion experiments; the volume fraction of crystalline phase was checked by the Mössbauer spectroscopy. Concentration profiles obtained by sputtering by Ar+ ions in a glow discharge show two distinct branches suggesting that two diffusion paths are operating. Arrhenius plot of measured diffusion coefficients was not linear in the whole temperature studied interval, which may be due to predominance of less energetically demanding jumps at lower temperatures and higher effective activation enthalpy at higher temperatures. The kink temperature was about 630 K.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

43

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

10

Strana od-do

338-347

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—