Hydrogen diffusion in hydrogenated Mg and Mg-Mg2Ni eutectic alloy

Popis výsledku v původním jazyce

Time dependence of total amount of hydrogen desorbed from hydrogen-charged Mg and eutectic Mg-Mg2Ni (23.5 wt.% Ni) alloy was measured at temperatures from interval 552?723 K. Experiments were carried out well below the equilibrium pressure, where these hydrides ? perspective as solid hydrogen storage media ? are unstable and the desorption process is controlled mainly by diffusion of hydrogen in respective hydride (MgH2 and/or Mg2NiH4). Hydrogen diffusion coefficients were evaluated from desorption curves and hydrogen diffusion coefficient along interphase boundary MgH2/Mg2NiH4 was estimated from results obtained with the eutectic alloy.

Název v anglickém jazyce

Hydrogen diffusion in hydrogenated Mg and Mg-Mg2Ni eutectic alloy

Popis výsledku anglicky

Time dependence of total amount of hydrogen desorbed from hydrogen-charged Mg and eutectic Mg-Mg2Ni (23.5 wt.% Ni) alloy was measured at temperatures from interval 552?723 K. Experiments were carried out well below the equilibrium pressure, where these hydrides ? perspective as solid hydrogen storage media ? are unstable and the desorption process is controlled mainly by diffusion of hydrogen in respective hydride (MgH2 and/or Mg2NiH4). Hydrogen diffusion coefficients were evaluated from desorption curves and hydrogen diffusion coefficient along interphase boundary MgH2/Mg2NiH4 was estimated from results obtained with the eutectic alloy.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0010" target="_blank" >GA106/07/0010: Difúze vodíku ve slitinách Mg-Ni modifikovaných vybranými prvky snižujícími stabilitu hydridů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

45

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

8

Strana od-do

305-312

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—