Kinetika vodíku v Mg2Ni a v hydrogenovaném eutektiku Mg-Mg2Ni

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00307737" target="_blank" >RIV/68081723:_____/08:00307737 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Kinetics of hydrogen in Mg2Ni and in hydrogenated Mg and Mg-Mg2Ni eutectic

Popis výsledku v původním jazyce

Time dependence of total amount of hydrogen desorbed from hydrogen-charged Mg and eutectic Mg-Mg2Ni (23.5 wt. % Ni) alloy was measured at temperatures from interval 552 ? 723 K. Experiments were carried out well below the equilibrium pressure, where these hydrides ? perspective as solid hydrogen storage media ? are unstable and the desorption process is controlled mainly by diffusion of hydrogen in respective hydride (MgH2 and/or Mg2NiH4). Hydrogen diffusion coefficients were evaluated from desorption curves and hydrogen diffusion coefficient along interphase boundary MgH2/Mg2NiH4 was estimated from results obtained with the eutectic alloy.

Název v anglickém jazyce

Kinetics of hydrogen in Mg2Ni and in hydrogenated Mg and Mg-Mg2Ni eutectic

Popis výsledku anglicky

Time dependence of total amount of hydrogen desorbed from hydrogen-charged Mg and eutectic Mg-Mg2Ni (23.5 wt. % Ni) alloy was measured at temperatures from interval 552 ? 723 K. Experiments were carried out well below the equilibrium pressure, where these hydrides ? perspective as solid hydrogen storage media ? are unstable and the desorption process is controlled mainly by diffusion of hydrogen in respective hydride (MgH2 and/or Mg2NiH4). Hydrogen diffusion coefficients were evaluated from desorption curves and hydrogen diffusion coefficient along interphase boundary MgH2/Mg2NiH4 was estimated from results obtained with the eutectic alloy.

Druh

D - Stať ve sborníku

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0010" target="_blank" >GA106/07/0010: Difúze vodíku ve slitinách Mg-Ni modifikovaných vybranými prvky snižujícími stabilitu hydridů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2008. Sborník přednášek.

ISBN

978-80-254-1987-8

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

13. 5. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—