Vliv elasticity krystalu na napjatost v povrchových zrnech polykrystalické austenitické korozivzdorné oceli. Srovnání s experimentem

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00305756" target="_blank" >RIV/68081723:_____/08:00305756 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of crystalline elasticity on the stress distribution at the free surface of an austenitic stainless steel polycrystal. Comparison with experiments

Popis výsledku v původním jazyce

This numerical study focuses on the recent AFM observations of Man et al. showing well-oriented grains in fatigued 316L austenitic stainless steel, however presenting no persistent slip markings (PSMs). Scanning electron microscopy (SEM) permits us to build finite element (FE) meshes of the observed grain aggregates and to assign to the modelled grains the crystallographic orientations measured by electron backscattering diffraction (EBSD). Then, 3D FE computations using the crystalline elasticity allowthe evaluation of mean grain stress tensors and resolved shear stresses. The results could explain qualitatively the anomalous behaviour of the studied well-oriented grains which is partly due to the particular orientations and shapes of the neighbour grains. This study highlights the influence of crystalline elasticity and neighbour grains in microplasticity and crack nucleation.

Název v anglickém jazyce

Influence of crystalline elasticity on the stress distribution at the free surface of an austenitic stainless steel polycrystal. Comparison with experiments

Popis výsledku anglicky

This numerical study focuses on the recent AFM observations of Man et al. showing well-oriented grains in fatigued 316L austenitic stainless steel, however presenting no persistent slip markings (PSMs). Scanning electron microscopy (SEM) permits us to build finite element (FE) meshes of the observed grain aggregates and to assign to the modelled grains the crystallographic orientations measured by electron backscattering diffraction (EBSD). Then, 3D FE computations using the crystalline elasticity allowthe evaluation of mean grain stress tensors and resolved shear stresses. The results could explain qualitatively the anomalous behaviour of the studied well-oriented grains which is partly due to the particular orientations and shapes of the neighbour grains. This study highlights the influence of crystalline elasticity and neighbour grains in microplasticity and crack nucleation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science Forum

ISSN

0255-5476

e-ISSN

—

Svazek periodika

567-568

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

149-152

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—