Fractural based microstructural damane evaluation in Ni-based superalloy gas turbine blades

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00358287" target="_blank" >RIV/68081723:_____/10:00358287 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fractural based microstructural damane evaluation in Ni-based superalloy gas turbine blades

Popis výsledku v původním jazyce

A fractal based evaluation of microstructural damage in Ni based superalloy cast IN 738 LC used in gas turbine blades is presented in the paper. Non-destructive in-situ replica method was used without damaging the blades for the evaluation of microstructure. The theoretical life of the stator blades of the gas turbine, which was exposed to temperature varying between 1060°C to 1100°C, was approximately 100,000 hours. In order to assess the suitability of the stator blades after 50% of the service life,fractal based microstructural damage evaluation has been conducted. The fractal dimensions of the in situ metallographic images can be correlated to the progressive deterioration of hardness at various locations of the blades. The extent of damage is inversely proportional to the fractal dimension. For fractal dimension below 2.4, the material can be classified as substantially damaged.

Název v anglickém jazyce

Fractural based microstructural damane evaluation in Ni-based superalloy gas turbine blades

Popis výsledku anglicky

A fractal based evaluation of microstructural damage in Ni based superalloy cast IN 738 LC used in gas turbine blades is presented in the paper. Non-destructive in-situ replica method was used without damaging the blades for the evaluation of microstructure. The theoretical life of the stator blades of the gas turbine, which was exposed to temperature varying between 1060°C to 1100°C, was approximately 100,000 hours. In order to assess the suitability of the stator blades after 50% of the service life,fractal based microstructural damage evaluation has been conducted. The fractal dimensions of the in situ metallographic images can be correlated to the progressive deterioration of hardness at various locations of the blades. The extent of damage is inversely proportional to the fractal dimension. For fractal dimension below 2.4, the material can be classified as substantially damaged.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New Methods of Damage and Failure Analysis of Structural Parts

ISBN

978-80-248-2265-5

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

—

Název nakladatele

VŠB - TU Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

6. 9. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—