Creep in directionally solidified NiAl-Mo eutectics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00375996" target="_blank" >RIV/68081723:_____/11:00375996 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26310/11:PU110742

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.scriptamat.2011.07.019" target="_blank" >http://dx.doi.org/10.1016/j.scriptamat.2011.07.019</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2011.07.019" target="_blank" >10.1016/j.scriptamat.2011.07.019</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Creep in directionally solidified NiAl-Mo eutectics

Popis výsledku v původním jazyce

A directionally solidified NiAl?Mo eutectic and an NiAl intermetallic, having respective nominal compositions Ni?45.5Al?9Mo and Ni?45.2Al (at.%), were loaded in compression at 1073 and 1173 K. Formidable strengthening by regularly distributed Mo fibres (average diameter 600 nm, volume fraction 14%) was observed. The fibres can support compression stresses transferred from the plastically deforming matrix up to a critical stress of the order of 2.5 GPa, at which point they yield. Microstructural evidenceis provided for the dislocation-mediated stress transfer from the NiAl to the Mo phase.

Název v anglickém jazyce

Creep in directionally solidified NiAl-Mo eutectics

Popis výsledku anglicky

A directionally solidified NiAl?Mo eutectic and an NiAl intermetallic, having respective nominal compositions Ni?45.5Al?9Mo and Ni?45.2Al (at.%), were loaded in compression at 1073 and 1173 K. Formidable strengthening by regularly distributed Mo fibres (average diameter 600 nm, volume fraction 14%) was observed. The fibres can support compression stresses transferred from the plastically deforming matrix up to a critical stress of the order of 2.5 GPa, at which point they yield. Microstructural evidenceis provided for the dislocation-mediated stress transfer from the NiAl to the Mo phase.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F09%2F2073" target="_blank" >GA202/09/2073: Deformační mechanismy in-situ kompozitních materiálů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

65

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

699-702

Kód UT WoS článku

000295109500013

EID výsledku v databázi Scopus

—