High Temperature Creep in a Zr-1wt.%Nb Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00450440" target="_blank" >RIV/68081723:_____/15:00450440 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High Temperature Creep in a Zr-1wt.%Nb Alloy
Popis výsledku v původním jazyce
This paper presents experimental results regarding high temperature behaviour of a Zr-1wt.%Nb alloy corresponding to LOCA situation of fuel cladding tubes for nuclear reactor. The tube exhibited equiaxed ? grains with an initial grain size of about 5 ?m.Constant stress uniaxial tensile creep tests were carried out at temperatures from 550 to 800° C over a wide range of the applied stress up to a true strain of about 40%. From the creep data was identified presence of power-law creep, which is dislocation climb controlled (self-diffusion controlled). Then the activation energy for creep Qc should be fairly consistent with that of self-diffusion. The determined activation energies of 243-269 kJ/mol fall within the range of self-diffusion activation energies.
Název v anglickém jazyce
High Temperature Creep in a Zr-1wt.%Nb Alloy
Popis výsledku anglicky
This paper presents experimental results regarding high temperature behaviour of a Zr-1wt.%Nb alloy corresponding to LOCA situation of fuel cladding tubes for nuclear reactor. The tube exhibited equiaxed ? grains with an initial grain size of about 5 ?m.Constant stress uniaxial tensile creep tests were carried out at temperatures from 550 to 800° C over a wide range of the applied stress up to a true strain of about 40%. From the creep data was identified presence of power-law creep, which is dislocation climb controlled (self-diffusion controlled). Then the activation energy for creep Qc should be fairly consistent with that of self-diffusion. The determined activation energies of 243-269 kJ/mol fall within the range of self-diffusion activation energies.
Klasifikace
Druh
O - Ostatní výsledky
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů