Assessment of dwell-fatigue properties of nickel-based superalloy coated with a multi-layered thermal and environmental barrier coating

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F25%3A00600387" target="_blank" >RIV/68081723:_____/25:00600387 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0142112324005528?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0142112324005528?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2024.108693" target="_blank" >10.1016/j.ijfatigue.2024.108693</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of dwell-fatigue properties of nickel-based superalloy coated with a multi-layered thermal and environmental barrier coating

Popis výsledku v původním jazyce

A three-layered experimental thermal and environmental barrier coating (TEBC) was deposited using air plasma spraying technology on cylindrical specimens of nickel-based superalloy MAR-M247. TEBC consists of mullite (Al6Si2O13) and hexacelsian (BaAl2Si2O8) upper layer, Y2O3 stabilised ZrO2 interlayer and CoNiCrAlY bond coat deposited on the grit-blasted surface of MAR-M247. The cyclic plastic response and damage mechanisms in uncoated and TEBC-coated MAR-M247 have been studied in isothermal dwell-fatigue tests conducted under strain control with constant strain amplitude at 900 °C. In each cycle, 5-minute dwells were introduced in both tensile and compression peaks of the hysteresis loop. Fatigue hardening/softening curves, stress relaxation curves, cyclic stress–strain curves and fatigue life curves are reported. Ceaseless mild softening has been found in both uncoated and TEBC-coated MAR-M247. TEBC-coated MAR-M247 showed an improved lifetime in the whole range of tested strain amplitudes. Data obtained from stress relaxation curves were used to assess the fraction of creep damage. The generalised damage accumulation rule was used to evaluate damage due to fatigue-creep-environment interaction. A study of the surface relief and internal microstructure using SEM and TEM helped to interpret the specifics of fatigue behaviour of uncoated and TEBC-coated material. The effectiveness of this newly developed TEBC, together with the dwell sensitivity of MAR-M247, were discussed from the perspective relevant to dwell-fatigue cyclic straining.

Název v anglickém jazyce

Assessment of dwell-fatigue properties of nickel-based superalloy coated with a multi-layered thermal and environmental barrier coating

Popis výsledku anglicky

A three-layered experimental thermal and environmental barrier coating (TEBC) was deposited using air plasma spraying technology on cylindrical specimens of nickel-based superalloy MAR-M247. TEBC consists of mullite (Al6Si2O13) and hexacelsian (BaAl2Si2O8) upper layer, Y2O3 stabilised ZrO2 interlayer and CoNiCrAlY bond coat deposited on the grit-blasted surface of MAR-M247. The cyclic plastic response and damage mechanisms in uncoated and TEBC-coated MAR-M247 have been studied in isothermal dwell-fatigue tests conducted under strain control with constant strain amplitude at 900 °C. In each cycle, 5-minute dwells were introduced in both tensile and compression peaks of the hysteresis loop. Fatigue hardening/softening curves, stress relaxation curves, cyclic stress–strain curves and fatigue life curves are reported. Ceaseless mild softening has been found in both uncoated and TEBC-coated MAR-M247. TEBC-coated MAR-M247 showed an improved lifetime in the whole range of tested strain amplitudes. Data obtained from stress relaxation curves were used to assess the fraction of creep damage. The generalised damage accumulation rule was used to evaluate damage due to fatigue-creep-environment interaction. A study of the surface relief and internal microstructure using SEM and TEM helped to interpret the specifics of fatigue behaviour of uncoated and TEBC-coated material. The effectiveness of this newly developed TEBC, together with the dwell sensitivity of MAR-M247, were discussed from the perspective relevant to dwell-fatigue cyclic straining.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Fatigue

ISSN

0142-1123

e-ISSN

1879-3452

Svazek periodika

191

Číslo periodika v rámci svazku

FEB

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

15

Strana od-do

108693

Kód UT WoS článku

001354497000001

EID výsledku v databázi Scopus

2-s2.0-85208231664