Hydrothermal Conditions Influence on Aluminous Cement Pastes with Metakaolin

Popis výsledku v původním jazyce

Following contribution focuses on the influence of hydrothermal curing conditions applied at early age of cement pastes and theirs reaction to elevated temperatures. Hydrothermal curing in the autoclave device (150°C, 0.45 MPa and 100% humidity) took place for 4 hours. Tested pastes were made from aluminous cement Secar®71 suitable for refractory composites. The cement pastes were modified by various amount of metakaolin (0%, 5%, 10% and 15% of cement weight). Benefit of hydrothermal curing lies in rapid increase of mechanical properties at the age of 1 day after production. Basic mechanical properties, fracture energy, dynamic modulus of elasticity were tested on specimens 40 x 40 x 160 mm exposed to 105 °C, 600 °C and 1000 °C for 3 hours.

Název v anglickém jazyce

Hydrothermal Conditions Influence on Aluminous Cement Pastes with Metakaolin

Popis výsledku anglicky

Following contribution focuses on the influence of hydrothermal curing conditions applied at early age of cement pastes and theirs reaction to elevated temperatures. Hydrothermal curing in the autoclave device (150°C, 0.45 MPa and 100% humidity) took place for 4 hours. Tested pastes were made from aluminous cement Secar®71 suitable for refractory composites. The cement pastes were modified by various amount of metakaolin (0%, 5%, 10% and 15% of cement weight). Benefit of hydrothermal curing lies in rapid increase of mechanical properties at the age of 1 day after production. Basic mechanical properties, fracture energy, dynamic modulus of elasticity were tested on specimens 40 x 40 x 160 mm exposed to 105 °C, 600 °C and 1000 °C for 3 hours.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP104%2F12%2F0791" target="_blank" >GAP104/12/0791: Vláknové kompozity na bázi cementu pro vysokoteplotní aplikace</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Central Europe towards Sustainable Building 2016 - Innovations for Sustainable Future

ISBN

978-80-271-0248-8

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

313-314

Název nakladatele

GRADA PUBLISHING

Místo vydání

Praha

Místo konání akce

Prague

Datum konání akce

22. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—