Kinetic analysis of illite dehydroxylation from differential scanning calorimetry

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F19%3A00338075" target="_blank" >RIV/68407700:21110/19:00338075 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1063/1.5114059" target="_blank" >https://doi.org/10.1063/1.5114059</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1063/1.5114059" target="_blank" >10.1063/1.5114059</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Kinetic analysis of illite dehydroxylation from differential scanning calorimetry

Popis výsledku v původním jazyce

The two-step dehydroxylation of illite is studied using the differential scanning calorimetry on powder samples with heating rates from 1 to 10 °C min-1 in a dynamic argon atmosphere. The values of apparent activation energy and pre-exponential factor are calculated using the Kissinger method. The determined values of apparent activation energy and pre-exponential factor for the trans-vacant layer dehydroxylation are (227 ± 6) kJ mol-1 and (2.87 ± 0.09)x1013 min-1, respectively. The results also show that this process can be characterized by a 1D diffusion-controlled reaction with instantaneous nucleation rate. For the cis-vacant layer dehydroxylation, the values of apparent activation energy and pre-exponential factor are (242 ± 10) kJ mol-1 and (5.37 ± 0.23)x1012 min-1, respectively. The value of the Avrami peak factor for this step indicates diffusion-controlled growth of the new phase with zero or decreasing nucleation rate.

Název v anglickém jazyce

Kinetic analysis of illite dehydroxylation from differential scanning calorimetry

Popis výsledku anglicky

The two-step dehydroxylation of illite is studied using the differential scanning calorimetry on powder samples with heating rates from 1 to 10 °C min-1 in a dynamic argon atmosphere. The values of apparent activation energy and pre-exponential factor are calculated using the Kissinger method. The determined values of apparent activation energy and pre-exponential factor for the trans-vacant layer dehydroxylation are (227 ± 6) kJ mol-1 and (2.87 ± 0.09)x1013 min-1, respectively. The results also show that this process can be characterized by a 1D diffusion-controlled reaction with instantaneous nucleation rate. For the cis-vacant layer dehydroxylation, the values of apparent activation energy and pre-exponential factor are (242 ± 10) kJ mol-1 and (5.37 ± 0.23)x1012 min-1, respectively. The value of the Avrami peak factor for this step indicates diffusion-controlled growth of the new phase with zero or decreasing nucleation rate.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

AIP Conference Proceedings, International Conference on Numerical Analysis and Applied Mathematics 2018, ICNAAM 2018

ISBN

978-0-7354-1854-7

ISSN

0094-243X

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

American Institute of Physics Inc.

Místo vydání

—

Místo konání akce

Rhodes

Datum konání akce

13. 9. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—