Identification of strain fields in pure Al and hybrid Ni/Al metal foams using X-ray microtomography under loading

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21260%2F16%3A00309708" target="_blank" >RIV/68407700:21260/16:00309708 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378297:_____/16:00466629

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1748-0221/11/11/C11017/pdf" target="_blank" >http://iopscience.iop.org/article/10.1088/1748-0221/11/11/C11017/pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1748-0221/11/11/C11017" target="_blank" >10.1088/1748-0221/11/11/C11017</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Identification of strain fields in pure Al and hybrid Ni/Al metal foams using X-ray microtomography under loading

Popis výsledku v původním jazyce

Hybrid foams are materials formed by a core from a standard open cell metal foam that is during the process of electrodeposition coated by a thin layer of different nanocrystalline metals. The material properties of the base metal foam are in this way modified resulting in higher plateau stress and, more importantly, by introduction of strain-rate dependence to its deformation response. In this paper, we used time-lapse X-ray micro-tomography for the mechanical characterization of Ni/Al hybrid foams (aluminium open cell foams with nickel coating layer). To fully understand the effects of the coating layer on the material’s effective properties, we compared the compressive response of the base uncoated foam to the response of the material with coating thickness of 50 and 75 µm. Digital volume correlation (DVC) was applied to obtain volumetric strain fields of the deforming micro-structure up to the densification region of the deforming cellular structure. The analysis was performed as a compressive mechanical test with simultaneous observation using X-ray radiography and tomography. A custom design experimental device was used for compression of the foam specimens in several deformation states directly in the X-ray setup. Planar X-ray images were taken during the loading phases and a X-ray tomography was performed at the end of each loading phase (up to engineering strain 22 %). The samples were irradiated using micro-focus reflection type X-ray tube and images were taken using a large area flat panel detector. Tomography reconstructions were used for an identification of a strain distribution in the foam using digital volumetric correlation. A comparison of the deformation response of the coated and the uncoated foam in uniaxial quasi-static compression is summarized in the paper.

Název v anglickém jazyce

Identification of strain fields in pure Al and hybrid Ni/Al metal foams using X-ray microtomography under loading

Popis výsledku anglicky

Hybrid foams are materials formed by a core from a standard open cell metal foam that is during the process of electrodeposition coated by a thin layer of different nanocrystalline metals. The material properties of the base metal foam are in this way modified resulting in higher plateau stress and, more importantly, by introduction of strain-rate dependence to its deformation response. In this paper, we used time-lapse X-ray micro-tomography for the mechanical characterization of Ni/Al hybrid foams (aluminium open cell foams with nickel coating layer). To fully understand the effects of the coating layer on the material’s effective properties, we compared the compressive response of the base uncoated foam to the response of the material with coating thickness of 50 and 75 µm. Digital volume correlation (DVC) was applied to obtain volumetric strain fields of the deforming micro-structure up to the densification region of the deforming cellular structure. The analysis was performed as a compressive mechanical test with simultaneous observation using X-ray radiography and tomography. A custom design experimental device was used for compression of the foam specimens in several deformation states directly in the X-ray setup. Planar X-ray images were taken during the loading phases and a X-ray tomography was performed at the end of each loading phase (up to engineering strain 22 %). The samples were irradiated using micro-focus reflection type X-ray tube and images were taken using a large area flat panel detector. Tomography reconstructions were used for an identification of a strain distribution in the foam using digital volumetric correlation. A comparison of the deformation response of the coated and the uncoated foam in uniaxial quasi-static compression is summarized in the paper.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Instrumentation

ISSN

1748-0221

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

1-7

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—