Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading

Popis výsledku v původním jazyce

A study of fatigue behaviour an Fe-28Al-3Cr-Ce (at%) based alloy was carried out on compact tension (CT) specimens 5 mm in thickness. The specimens were loaded in tension at 20, 300 and 500°C with 10 Hz frequency and R in the range from 0.05 to 0.1.The fatigue crack growth rate was measured by the potential method. The number of cycles to failure decreases rapidly with temperature. The fatigue crack propagation rate at RT and elevated temperatures is different. The slope of v(DK) curves is much steeperat RT, while it remains almost the same at 300 and 500°C. The fatigue crack growth rate at 500°C is nearly two orders higher than at 300°C. Fractographic analysis showed that at room temperature fatigue crack growth is controlled by several mechanisms. The main failure mechanism is transgranular cleavage, crack growth by the brittle or ductile striation mechanism is localized only in several areas along the crack front.

Název v anglickém jazyce

Behaviour of an Fe-28Al-3Cr-Ce Alloy under Cyclic Loading

Popis výsledku anglicky

A study of fatigue behaviour an Fe-28Al-3Cr-Ce (at%) based alloy was carried out on compact tension (CT) specimens 5 mm in thickness. The specimens were loaded in tension at 20, 300 and 500°C with 10 Hz frequency and R in the range from 0.05 to 0.1.The fatigue crack growth rate was measured by the potential method. The number of cycles to failure decreases rapidly with temperature. The fatigue crack propagation rate at RT and elevated temperatures is different. The slope of v(DK) curves is much steeperat RT, while it remains almost the same at 300 and 500°C. The fatigue crack growth rate at 500°C is nearly two orders higher than at 300°C. Fractographic analysis showed that at room temperature fatigue crack growth is controlled by several mechanisms. The main failure mechanism is transgranular cleavage, crack growth by the brittle or ductile striation mechanism is localized only in several areas along the crack front.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0687" target="_blank" >GA106/02/0687: Úprava vlastností intermetalik na bázi Fe3Al termomechanickým zpracováním a aditivy</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Alloys and Compounds

ISSN

0925-8388

e-ISSN

—

Svazek periodika

378

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

263-267

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—