Lomové chování slitiny Fe3Al s přísadou Zr a C za různých teplot

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F05%3A04108232" target="_blank" >RIV/68407700:21340/05:04108232 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures

Popis výsledku v původním jazyce

The static and fatigue behaviour of hot rolled Fe-31.5Al-3.5Cr (at%) with addition of zirconium and carbon was studied at different temperatures. The tensile deformation tests were carried out at temperatures ranging from 20 to 600°C. The fatigue crack growth rate (v-deltaK ) curves were measured at 20, 300 and 500°C. The best fatigue crack growth resistance was reached at 300°C, while at 500°C the crack growth rate was the highest and the fatigue life the shortest. The predominant fatigue fracture mechanism is transgranular cleavage. However, a number of other micromorphologic features corresponding to various fracture mechanisms were observed: transgranular quasi-cleavage facets, ductile fatigue striations and brittle striations.

Název v anglickém jazyce

Fracture behaviour of Fe3Al alloy with additions of Zr and C at different temperatures

Popis výsledku anglicky

The static and fatigue behaviour of hot rolled Fe-31.5Al-3.5Cr (at%) with addition of zirconium and carbon was studied at different temperatures. The tensile deformation tests were carried out at temperatures ranging from 20 to 600°C. The fatigue crack growth rate (v-deltaK ) curves were measured at 20, 300 and 500°C. The best fatigue crack growth resistance was reached at 300°C, while at 500°C the crack growth rate was the highest and the fatigue life the shortest. The predominant fatigue fracture mechanism is transgranular cleavage. However, a number of other micromorphologic features corresponding to various fracture mechanisms were observed: transgranular quasi-cleavage facets, ductile fatigue striations and brittle striations.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0687" target="_blank" >GA106/02/0687: Úprava vlastností intermetalik na bázi Fe3Al termomechanickým zpracováním a aditivy</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

43

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

11

Strana od-do

134-144

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—